| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 物理性能 | 玻纖含量 | 30 | % | |||
| 比重 | ASTM D792 | 1.63 | ||||
| 熔點(diǎn) | DSC | 225 | ℃ | |||
| 機(jī)械性能 | 拉伸強(qiáng)度 | ASTM D638 | 1100 | kg/cm2 | ||
| 拉伸伸長率 | ASTM D638 | 3.2 | % | |||
| 彎曲強(qiáng)度 | ASTM D790 | 1700 | kg/cm2 | |||
| 彎曲模量 | ASTM D790 | 85000 | kg/cm2 | |||
| Izod缺口沖擊強(qiáng)度 | ASTM D256 | 8.0 | kg.cm/cm | |||
| 洛氏硬度 | ASTM D785 | 121 | R | |||
| 電氣性能 | 介電強(qiáng)度 | ASTM D149 | 22 | KV/mm | ||
| 體積電阻率 | ASTM D257 | 1015 | Ω.cm | |||
| 表面電阻率 | ASTM D257 | 1013 | Ω | |||
| 介電常數(shù) | 60Hz | ASTM D150 | 3.5 | |||
| 介電損耗因數(shù) | 60Hz | ASTM D150 | 0.001 | |||
| 耐電弧性 | ASTM D495 | 100 | SEC | |||
| 熱性能 | 熱變形溫度 | - | 1.8Mpa | ASTM D648 | 200 | ℃ |
| - | 0.46Mpa | ASTM D648 | 218 | ℃ | ||
| 阻燃性 | UL94 | V-0 | ||||