Hostab® S 27072 WS 10/1570
聚甲醛（POM）共聚物
Celanese Corporation
產(chǎn)品說明:
Chemical abbreviation according to ISO 1043-1: POM-HI
Molding compound ISO 9988- POM-K, M-GCLP, 05-001
Modified POM copolymer
Easy flowing, elastomer-containing injection molding type in color
modifying black 10/1570; especially weathering resistant; lower
chemical resistance than the basic type HOSTAFORM C 27021; high
resistance to thermal and oxidative degradation.
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: for molded parts with matt surface.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
|
供貨地區(qū) |
|
|||||
|
特性 |
|
|||||
|
RoHS 合規(guī)性 |
聯(lián)系制造商 |
|||||
|
外觀 |
黑色 |
|||||
|
加工方法 |
注射成型 |
|||||
|
樹脂ID (ISO 1043) |
POM-HI |
|||||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
|
密度 |
1.39 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
21.0 |
cm3/10min |
ISO 1133 |
|||
|
吸水率 (飽和, 23°C) |
0.70 |
% |
ISO 62 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
2000 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
46.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
8.0 |
% |
ISO 527-2/1A/50 |
|
標(biāo)稱拉伸斷裂應(yīng)變 |
35 |
% |
ISO 527-2/1A/50 |
|
拉伸蠕變模量 |
|
|
ISO 899-1 |
|
1 hr |
1800 |
MPa |
|
|
1000 hr |
1000 |
MPa |
|
|
彎曲模量 (23°C) |
2100 |
MPa |
ISO 178 |
|
沖擊性能 |
額定值 |
單位制 |
測試方法 |
|
簡支梁缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eA |
|
-30°C |
8.0 |
kJ/m2 |
|
|
23°C |
11 |
kJ/m2 |
|
|
簡支梁無缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eU |
|
-30°C |
110 |
kJ/m2 |
|
|
23°C, 局部斷裂 |
150 |
kJ/m2 |
|
|
熱性能 |
額定值 |
單位制 |
測試方法 |
|
熱變形溫度 (1.8 MPa, 未退火) |
84.0 |
°C |
ISO 75-2/A |
|
熔融溫度 3 |
166 |
°C |
ISO 11357-3 |
|
線形熱膨脹系數(shù) - 流動(dòng) |
1.2E-4 |
cm/cm/°C |
ISO 11359-2 |
|
|