Hostab® MT8F01
聚甲醛（POM）共聚物
Celanese Corporation
產(chǎn)品說(shuō)明:
Hostab® acetal copolymer grade MT8F01 is a special grade developed for medical industry applications containing low residual monomers. Hostab® MT8F01 is a standard flow low level polytetrafluoroethylene filled (PTFE) product designed for use in wear applications against plastics, bl, glass or ceramic mating surfaces where silicone lubricants can not be tolerated.
|
供貨地區(qū) |
|
|||||
|
添加劑 |
PTFE潤(rùn)滑劑 |
|||||
|
用途 |
醫(yī)療/護(hù)理用品 |
|||||
|
RoHS 合規(guī)性 |
聯(lián)系制造商 |
|||||
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|||
|
密度 |
1.44 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
7.90 |
cm3/10min |
ISO 1133 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 |
2600 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
58.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
9.0 |
% |
ISO 527-2/1A/50 |
|
標(biāo)稱拉伸斷裂應(yīng)變 |
28 |
% |
ISO 527-2/1A/50 |
|
沖擊性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 (23°C) |
5.2 |
kJ/m2 |
ISO 179/1eA |
|
熱性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
熱變形溫度 (1.8 MPa, 未退火) |
102 |
°C |
ISO 75-2/A |
|
熔融溫度 2 |
166 |
°C |
ISO 11357-3 |
|
線形熱膨脹系數(shù) |
|
|
ISO 11359-2 |
|
流動(dòng) |
1.2E-4 |
cm/cm/°C |
|
|
橫向 |
1.2E-4 |
cm/cm/°C |
|
|
|