Hostab® M10AE
聚甲醛（POM）共聚物
Celanese Corporation
產(chǎn)品說明:
POM copolymer
Stiff-flowing type with high melt strength; good chemical resistance
to solvents, fuel and strong alkalis as well as good hydrolysis
resistance; high resistance to thermal and oxidative degradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011
FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more
than 1 mm.
Ranges of applications: For extrusion blow molding, and for
injection molding thick-walled, void-free molded parts.
|
特性 |
|
|||||
|
用途 |
|
|||||
|
機(jī)構(gòu)評(píng)級(jí) |
|
|||||
|
RoHS 合規(guī)性 |
聯(lián)系制造商 |
|||||
|
加工方法 |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|||
|
密度 |
1.41 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
0.900 |
cm3/10min |
ISO 1133 |
|||
|
吸水率 (飽和, 23°C) |
0.65 |
% |
ISO 62 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 |
2800 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
65.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
9.0 |
% |
ISO 527-2/1A/50 |
|
標(biāo)稱拉伸斷裂應(yīng)變 |
25 |
% |
ISO 527-2/1A/50 |
|
拉伸蠕變模量 |
|
|
ISO 899-1 |
|
1 hr |
2400 |
MPa |
|
|
1000 hr |
1200 |
MPa |
|
|
沖擊性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eA |
|
-30°C |
8.0 |
kJ/m2 |
|
|
23°C |
10 |
kJ/m2 |
|
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eU |
|
-30°C |
200 |
kJ/m2 |
|
|
23°C, 局部斷裂 |
220 |
kJ/m2 |
|
|
熱性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
熱變形溫度 (1.8 MPa, 未退火) |
97.0 |
°C |
ISO 75-2/A |
|
熔融溫度 2 |
167 |
°C |
ISO 11357-3 |
|
線形熱膨脹系數(shù) - 流動(dòng) |
1.3E-4 |
cm/cm/°C |
ISO 11359-2 |
|
|