Hostab® LX90Z XAP2 ?
聚甲醛（POM）共聚物
Celanese Corporation
產(chǎn)品說明:
Preliminary Data Sheet
Hostab® acetal copolymer grade LX90Z XAP2 ? is UV stabilized material available in a range of molded in bllic colors generally for automotive interior applications. In addition, Hostab® LX90Z XAP2 ? has lower volatile emissions as required for some automotive interiors.
Besides material, optimal finish for specialty bllic parts is dependent on proper drying, gate design, knit line bs, and special processing. Please contact Celanese Technical Service for assistance with your application.
Low Emission Perbance [VDA-275] <5 PPM
|
供貨地區(qū) |
|
|||||
|
添加劑 |
紫外線穩(wěn)定劑 |
|||||
|
特性 |
低揮發(fā) |
|||||
|
用途 |
|
|||||
|
RoHS 合規(guī)性 |
聯(lián)系制造商 |
|||||
|
外觀 |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
|
密度 |
1.43 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
8.00 |
cm3/10min |
ISO 1133 |
|||
|
收縮率 |
|
|
ISO 294-4 |
|||
|
橫向流量 |
1.4 |
% |
|
|||
|
流量 |
2.3 |
% |
|
|||
|
吸水率 (飽和, 23°C) |
0.75 |
% |
ISO 62 |
|||
|
機械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
2700 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
54.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
8.0 |
% |
ISO 527-2/1A/50 |
|
彎曲模量 (23°C) |
2900 |
MPa |
ISO 178 |
|
|
|
|
|