Hostab® C 9021 TF
聚甲醛（POM）共聚物
Celanese Corporation
產(chǎn)品說(shuō)明:
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNS, 02-002
POM copolymer
Injection molding type, modified with PTFE; good
chemical resistance to solvents, fuel and strong alkalis as well as
good hydrolysis resistance; high resistance to thermal and oxidative
degradation; for sliding combinations with very low coefficient of
friction.
UL-registration in natural and a thickness more than 1.57 mm as UL
94 HB, temperature index UL 746 B electrical 105°C, mechanical
95°C (tensile impact) and 100°C (tensile).
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: For sliding combinations with very low
coefficient of friction.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
UL = Underwriters Laboratories (USA)
|
供貨地區(qū) |
|
|||||
|
添加劑 |
|
|||||
|
特性 |
|
|||||
|
RoHS 合規(guī)性 |
|
|||||
|
加工方法 |
|
|||||
|
樹(shù)脂ID (ISO 1043) |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測(cè)試方法 |
|||
|
密度 |
1.51 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
6.00 |
cm3/10min |
ISO 1133 |
|||
|
收縮率 |
|
|
ISO 294-4 |
|||
|
橫向流量 |
1.7 |
% |
|
|||
|
流量 |
2.0 |
% |
|
|||
|
吸水率 (飽和, 23°C) |
0.65 |
% |
ISO 62 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
拉伸模量 |
2500 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
48.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
7.0 |
% |
ISO 527-2/1A/50 |
|
標(biāo)稱拉伸斷裂應(yīng)變 |
16 |
% |
ISO 527-2/1A/50 |
|
拉伸蠕變模量 |
|
|
ISO 899-1 |
|
1 hr |
2100 |
MPa |
|
|
1000 hr |
1200 |
MPa |
|
|
彎曲模量 (23°C) |
2400 |
MPa |
ISO 178 |
|
沖擊性能 |
額定值 |
單位制 |
測(cè)試方法 |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eA |
|
-30°C |
4.0 |
kJ/m2 |
|
|
23°C |
4.0 |
kJ/m2 |
|
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
|
ISO 179/1eU |
|
-30°C |
60 |
kJ/m2 |
|
|
23°C |
60 |
kJ/m2 |
|
|
|
|||