Hostab® C 9021 AW XAP2 ? LS
聚甲醛（POM）共聚物
Celanese Corporation
產(chǎn)品說明:
POM copolymer
Injection molding type like C 9021, with special additive modified;
good chemical resistance to solvents, fuel and strong alkalis as
well as good hydrolysis resistance; high resistance to thermal and
oxidative degradation; good wear properties and low coefficient of
friction.
Reduced emission grade. Emissions according to VDA 275 < 5 mg/kg
Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness
more than 1 mm.
Ranges of applications: sliding parts for b lifter.
FMVSS = Federal Motor Vehicle Safety Standard (USA)
Preliminary Data Sheet
|
添加劑 |
|
|||||
|
特性 |
|
|||||
|
RoHS 合規(guī)性 |
|
|||||
|
加工方法 |
|
|||||
|
物理性能 |
額定值 |
單位制 |
測試方法 |
|||
|
密度 |
1.38 |
g/cm3 |
ISO 1183 |
|||
|
溶化體積流率（MVR） (190°C/2.16 kg) |
8.00 |
cm3/10min |
ISO 1133 |
|||
|
收縮率 |
|
|
ISO 294-4 |
|||
|
橫向流量 |
1.6 |
% |
|
|||
|
流量 |
1.8 |
% |
|
|||
|
吸水率 (飽和, 23°C) |
0.65 |
% |
ISO 62 |
|||
|
機(jī)械性能 |
額定值 |
單位制 |
測試方法 |
|
拉伸模量 |
2450 |
MPa |
ISO 527-2/1A/1 |
|
拉伸應(yīng)力 (屈服) |
57.0 |
MPa |
ISO 527-2/1A/50 |
|
拉伸應(yīng)變 (屈服) |
8.0 |
% |
ISO 527-2/1A/50 |
|
標(biāo)稱拉伸斷裂應(yīng)變 |
20 |
% |
ISO 527-2/1A/50 |
|
彎曲模量 (23°C) |
2150 |
MPa |
ISO 178 |
|
|
|
|
|