| 分類: | E9018-G, SFA/AWS A5.5, E 55 6 Mn1NiMo B T 32 H5, EN ISO 18275-A |
| 認(rèn)證: | E9018-G, ABS, 3.2 - 4.0 mm, NAKS/HAKC, UNA 272581, Seproz |
Approvals are based on factory b. Please contact ESAB for more inbation.
| Alloy Type: | C, Mn, 1% Ni |
| Coating Type: | Basic |
| Diffusible Hydrogen: | <5.0 ml/100g |
| Welding Current: | AC, DC+- |
| Impact Value | Testing Temperature |
| ISO PWHT 580°C 1h | |
| 80 J | -50 °C |
| 60 J | -60 °C |
| Elongation | Tensile Strength | Yield Strength | Stress Relieved Temperature | Stress Relieved Testing Time |
| ISO PWHT 580°C 1h | ||||
| 21 % | 710 MPa | 650 MPa | - | - |
| AWS Stress relieved | ||||
| - | - | - | 620 °C | 1 hr |
| Fusion time per electrode at 90% I max | kg weld bl/kg electrodes | Number of electrodes/kg weld bl | 安培 | 熔敷率 | 電壓 V | 直徑 |
| 60 hr | 0.60 kg | 83.3 | 55-85 A | 0.72 kg/h | 24.4 V | 2.5 x 350 mm |
| 68 hr | 0.55 kg | 56.6 | 80-140 A | 0.94 kg/h | 23.3 V | 3.2 x 350 mm |
| 103 hr | 0.60 kg | 24.4 | 120-180 A | 1.43 kg/h | 24.0 V |
4.0 x 450 mm |