規(guī)格
| EN 14700 |
| T Fe1 |
| 電流類型 CA/CD/CC (+)(-) | DC+ |
| 硬度 (HRC) | 32-40 HRC |
| 元素 | C |
| 元素 | Si |
| 額定百分比 | 1 % |
| 安培 | 250-450 A |
| 電壓 V | 28-38 V |
| 直徑 | 2.4 mm |
| 安培 | 500-900 A |
| 電壓 V | 28-34 V |
| 直徑 | 4 mm |
| 送絲速度 | 2.0-5.0 m/min |
OK Tubrodur 15.40S is a flux-cored wire for SAW hardfacing in conjunction with OK Flux 10.71, depositing a manganese-chromium-molybdenum-alloyed weld bl with a hardness of 32-36 Rockwell C. Suitable for surfacing wheel runners, track bs, wheels and rollers for conveyor belts, wheels for mine trucks, rolls and shafts, where a hardness within the range of 32-40 Rockwell C is desired. With negative polarity, less heat b to the base material, less dilution of the weld bl and a higher deb rate are obtained. In most cases, surfacing with OK Tubrodur 15.40S can be perbed without preheat. The need for preheat and increased interpass temperature is determined by the weldability of the parent material in question and the b and dimensions of the workpiece. Whenever possible, surfaced axles and similar bs, which are exposed to a bending stress during rotation, should always be stress relieved at 500-600°C.