INCOFLUXR SAS1 帶極埋弧焊劑
INCOFLUX SAS1 帶極埋弧焊劑設(shè)計(jì)與INCONEL 82／625帶狀焊接電極匹配使用。這種焊劑與這兩種合金電極匹配，可以用于碳鋼的表面堆焊。這種中性的燒結(jié)焊劑使第二層堆焊金屬的化學(xué)成分與電極的化學(xué)成分非常近似。盡管沒(méi)有電磁操控作用，但熔融焊劑平滑致密的紋理和良好的潤(rùn)濕性仍可以保證堆焊層的平整。
|
焊接參數(shù)：應(yīng)用DCEP電流方式 |
||||||
|
電極尺寸 |
電流／安培 |
電壓／伏特 |
焊接速度 |
電極干伸長(zhǎng) |
焊劑層厚度 |
|
|
0.5×60mm |
700-900 |
25-28 |
4-5 in/min 100-125mm/min |
0.75-1 in 19-25 mm |
0.75-1.5 in 19-38 mm |
|
|
0.5×30mm |
300-450 |
25-28 |
4-5 in/min 100-125mm/min |
0.75-1 in 19-25 mm |
0.75-1.5 in 19-38 mm |
|
儲(chǔ)藏和干燥條件
焊劑密封在未開(kāi)啟的容器中可以無(wú)限期保存。如果焊劑暴露于潮濕環(huán)境中，可以在500oF保溫烘干2小時(shí)或600oF保溫烘干1小時(shí)后使用。未熔化的焊劑若要回收利用，應(yīng)當(dāng)與新的焊劑按1／1的比例混合后再使用。
|
焊劑顆粒尺寸 泰勒制網(wǎng)目：10×100目
|
|
包裝 桶蓋上帶有橡膠密封墊圈的60磅聚乙烯桶密封包裝
|
The design of INCOFLUX SAS1 belt is designed with INCONEL 82/625 welding electrodes. The flux is matched with these two alloy electrodes and can be used for surfacing of carbon steel. This neutral sintering flux makes the chemical comb of the second layer surfacing bl approximate to the chemical comb of the electrode. Although there is no electromagnetic manipulation, the smooth and dense texture of melt flux and good wettability can guarantee the bation of the surfacing layer.
Welding beters: applying DCEP current mode
Electrode size current/ampere voltage/v welding speed electrode dry extension flux layer thickness
0.5 x 60mm 700-900 25-284-5 in/min
In 100-125 - mm/min 0.75-1
0.75 1.5 in 19-25 mm
19-38 mm
0.5 x 30mm 300-450 25-28 4-5 in/min
In 100-125 - mm/min 0.75-1
0.75 1.5 in 19-25 mm
19-38 mm
Storage and drying conditions
The flux seals can be kept indefiniby in unopened containers. If the solder is exposed to wet conditions, it can be used after an hour of thermal insulation drying for 2 hours or 600oF. If the unmelted flux is to be recycled, it should be mixed with the new flux at 1/1.
Flux particle size
Taylor's mesh: 10 times 100
packaging
The barrel cover is covered with a 60 - pound polyethylene barrel sealed with rubber gasketINCOFLUX SAS1 帶極埋弧焊劑設(shè)計(jì)與INCONEL 82／625帶狀焊接電極匹配