INCOFLUXR ESS10 帶極電渣焊劑
INCOFLUX ESS10 帶極電渣焊劑設(shè)計(jì)與INCONEL 82／622／625和INCO-WELD C-276／686CPT帶狀焊接電極匹配使用。這種焊劑與這些合金電極匹配，可以用于碳鋼的表面電渣堆焊。這種中性的燒結(jié)焊劑和電渣焊接過(guò)程使第二層堆焊金屬的稀釋率較低，其化學(xué)成分與電極的化學(xué)成分非常近似。盡管沒(méi)有電磁操控作用，但熔融焊劑平滑致密的紋理和良好的潤(rùn)濕性仍可以保證堆焊層的平整。
|
焊接參數(shù)：應(yīng)用DCEP電流方式 |
||||||
|
電極尺寸 |
電流／安培 |
電壓／伏特 |
焊接速度 |
電極干伸長(zhǎng) |
焊劑層厚度 |
|
|
0.5×60mm |
1100-1300 |
23-24 |
6-7 in/min 150-175mm/min |
0.75-1 in 19-25 mm |
0.75-1.5 in 19-38 mm |
|
|
0.5×30mm |
600-700 |
23-24 |
6-7 in/min 150-175mm/min |
0.75-1 in 19-25 mm |
0.75-1.5 in 19-38 mm |
|
儲(chǔ)藏和干燥條件
焊劑密封在未開(kāi)啟的容器中可以無(wú)限期保存。如果焊劑暴露于潮濕環(huán)境中，可以在400oF保溫烘干2小時(shí)或500oF保溫烘干1小時(shí)后使用。
|
焊劑顆粒尺寸 泰勒制網(wǎng)目：12×68目
|
|
包裝 88磅（40Kg）聚乙烯袋包裝
|
INCOFLUX ESS10 band electrode welding electrode was designed to match INCONEL 82/622/625 and INCO-WELD c-276/686cpt band welding electrode. The flux is matched with these alloy electrodes and can be used for surfacing of carbon steel surface. This neutral sintering flux and electroslag welding process makes the dilution rate of the second layer of welding bl low, and its chemical comb is very similar to the chemical comb of the electrode. Although there is no electromagnetic manipulation, the smooth and dense texture of melt flux and good wettability can guarantee the bation of the surfacing layer.
Welding beters: applying DCEP current mode
Electrode size current/ampere voltage/v welding speed electrode dry extension flux layer thickness
0.5 x 60mm 1100-1300 23-24 6-7 in/min
In 150-175 - mm/min 0.75-1
0.75 1.5 in 19-25 mm
19-38 mm
0.5 x 30mm 600-700 23-246-7 in/min
In 150-175 - mm/min 0.75-1
0.75 1.5 in 19-25 mm
19-38 mm
Storage and drying conditions
The flux seals can be kept indefiniby in unopened containers. If the flux is exposed to humid environment, it can be used after an hour or so of heat preservation for 2 hours or 500oF heat preservation.
Flux particle size
Taylor's mesh: 12 by 68 eyes
packaging
88-pound (40Kg) polyethylene bag packagingINCOFLUX ESS10 帶極電渣焊劑12×68目