INCOFLUXR 6 埋弧焊劑
INCOFLUX 6 埋弧焊劑是一種燒結(jié)焊劑，設(shè)計(jì)與INCONEL 61／82、NI-ROD 44和NILO CF36 焊絲匹配使用。這種焊劑的典型應(yīng)用是Nickel 200合金自身之間或與鋼之間的開(kāi)坡口焊接，以及與INCONEL 61匹配使用在碳鋼表面進(jìn)行堆焊。這種焊劑也可以與INCONEL 82填充金屬相匹配，形成多達(dá)三層的堆焊層。（注意：如果需要更多的堆焊層，應(yīng)當(dāng)使用INCOFLUX 4埋弧焊劑INCONEL 82填充金屬）。NI-ROD 44填充金屬和INCOFLUX 6 埋弧焊劑匹配可以用于鑄鐵之間以及鑄鐵和鋼之間的埋弧焊接。INCOFLUX 6 埋弧焊劑也可以與NILO CF36填充金屬匹配用于INVAR合金和NILO 36合金的焊接。
|
焊接參數(shù)：開(kāi)坡口焊或堆焊：應(yīng)用DCEP電流方式和窄焊道 |
||||||
|
焊絲直徑 |
電流／安培 |
電壓／伏特 |
焊接速度 |
電極干伸長(zhǎng) |
焊劑層厚度 |
|
|
0.062 in 1.6 mm |
250 |
28-30 |
10-12 in/min 250-305mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
250-300 |
30-33 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
|
電極擺動(dòng)堆焊：應(yīng)用DCEN電流方式，當(dāng)焊絲直徑為0.062 in時(shí)，擺動(dòng)頻率為50-70周／分；當(dāng)焊絲直徑為0.093 in時(shí)，擺動(dòng)頻率為35-60周／分 |
||||||
|
0.062 in 1.6 mm |
240-260 |
32-34 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
300-400 |
34-37 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
儲(chǔ)藏和干燥條件
焊劑密封在未開(kāi)啟的容器中可以無(wú)限期保存。如果焊劑暴露于潮濕環(huán)境中，可以在500oF保溫烘干2小時(shí)或600oF保溫烘干1小時(shí)后使用。
|
焊劑顆粒尺寸 泰勒制網(wǎng)目：10×100目
|
|
包裝 桶蓋上帶有橡膠密封墊圈的60磅聚乙烯桶密封包裝
|
The INCOFLUX 6 submerged arc welding agent is a sinter welding flux which is designed to match INCONEL 61/82, ni-rod 44 and NILO CF36 welding wire. The typical application of this kind of flux is Nickel 200 alloy itself between or between steel and the open groove welding, and INCONEL 61 matching USES on carbon steel surface for surfacing. The flux can also be matched with the INCONEL 82 filler bl, bing up to three layers of surfacing. (note: if more layers are needed, INCOFLUX 4 submerged arc welding agent INCONEL 82 should be used. Ni-rod 44 filler bl and INCOFLUX 6 submerged arc welding agent can be used for the submerged arc welding between cast iron and steel and steel. The INCOFLUX 6 submerged arc welding agent can also be used to match the NILO CF36 filler bl for the welding of INVAR alloy and NILO 36 alloy.
Welding beters: open groove welding or surfacing: apply DCEP current and narrow weld path
Electrode dry extension flux layer thickness of wire diameter current/ampere voltage/v welding speed electrode
0.062 in
1.6 mm 250 28-30 10-12 in/min
In 250-305 - mm/min 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 250-300 30-33 8-11 in/min
In 200-280 - mm/min 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Electrode swing surfacing welding: the use of DCEN current mode, when the wire diameter is 0.062 in, the oscillation frequency is 50-70 weeks/min; When the wire diameter is 0.093 in, the oscillation frequency is 35-60 weeks/min
0.062 in
1.6 mm 240-2632-34 4 in/min
100 mm/min in 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 300-400 34-37 4 in/min
100 mm/min in 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Storage and drying conditions
The flux seals can be kept indefiniby in unopened containers. If the solder is exposed to wet conditions, it can be used after an hour of thermal insulation drying for 2 hours or 600oF.
Flux particle size
Taylor's mesh: 10 times 100
packaging
The barrel cover is covered with a 60 - pound polyethylene barrel sealed with rubber gasket