INCOFLUXR 4 埋弧焊劑
INCOFLUX 4 埋弧焊劑是一種燒結(jié)焊劑，設(shè)計(jì)與INCONEL 82焊絲匹配使用，INCONEL 82焊絲是一種含鉻20％的高鎳合金。這種焊劑的典型應(yīng)用是INCONEL600／601合金、INCOLOY 800合金相互之間及它們與鐵素體金屬材料之間的開(kāi)坡口焊接。這種焊絲和焊劑的匹配尤其適用于碳鋼與不銹鋼之間的焊接，因?yàn)槠淙鄯蠼饘倬哂凶顑?yōu)的熱脹系數(shù)。這種焊劑的另一個(gè)主要應(yīng)用是與INCONEL 82填充金屬相匹配，在碳鋼表面堆焊形成耐蝕耐氧化層。
|
焊接參數(shù)：開(kāi)坡口焊或堆焊：應(yīng)用DCEP電流方式和窄焊道
|
||||||
|
焊絲直徑 |
電流／安培 |
電壓／伏特 |
焊接速度 |
電極干伸長(zhǎng) |
焊劑層厚度 |
|
|
0.062 in 1.6 mm |
240-290 |
30-33 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
250-300 |
30-33 |
8-11 in/min 200-280mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
|
電極擺動(dòng)堆焊：應(yīng)用DCEN電流方式，當(dāng)焊絲直徑為0.062 in時(shí)，擺動(dòng)頻率為50-70周／分；當(dāng)焊絲直徑為0.093 in時(shí)，擺動(dòng)頻率為35-60周／分 |
||||||
|
0.062 in 1.6 mm |
240-260 |
32-34 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
1/2-1 in 13-25 mm |
|
|
0.093 in 2.4mm |
300-400 |
34-37 |
4 in/min 100mm/min |
7/8-1 in 22-25 mm |
3/4-5/4 in 19-32 mm |
|
儲(chǔ)藏和干燥條件
焊劑密封在未開(kāi)啟的容器中可以無(wú)限期保存。如果焊劑暴露于潮濕環(huán)境中，可以在500oF保溫烘干2小時(shí)或600oF保溫烘干1小時(shí)后使用。
|
焊劑顆粒尺寸 泰勒制網(wǎng)目：10×100目
|
|
包裝
桶蓋上帶有橡膠密封墊圈的60磅聚乙烯桶密封包裝
|
The INCOFLUX 4 submerged arc welding agent is a sintering flux, which is designed to be used with INCONEL 82 welding wire. INCONEL 82 welding wire is a high nickel alloy with 20 % chromium. The typical application of this flux is INCONEL600/601 alloy, INCOLOY 800 alloy, and their welding between them and ferritic bl materials. This kind of wire and flux matching is especially suitable for welding between carbon steel and stainless steel because of its optimal thermal expansion coefficient. Another major application of this flux is the matching of the INCONEL 82 filler bl to the surface of carbon steel.
Welding beters: open groove welding or surfacing: apply DCEP current and narrow weld path
Electrode dry extension flux layer thickness of wire diameter current/ampere voltage/v welding speed electrode
0.062 in
1.6 mm 240-290 30-33 8-11 in/min
In 200-280 - mm/min 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 250-300 30-33 8-11 in/min
In 200-280 - mm/min 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Electrode swing surfacing welding: the use of DCEN current mode, when the wire diameter is 0.062 in, the oscillation frequency is 50-70 weeks/min; When the wire diameter is 0.093 in, the oscillation frequency is 35-60 weeks/min
0.062 in
1.6 mm 240-2632-34 4 in/min
100 mm/min in 7/8-1
1/2-1 in 22 to 25 mm
13 to 25 mm
0.093 in
2.4mm 300-400 34-37 4 in/min
100 mm/min in 7/8-1
22-25 mm 3/4-5/4 in
19 to 32 mm
Storage and drying conditions
The flux seals can be kept indefiniby in unopened containers. If the solder is exposed to wet conditions, it can be used after an hour of thermal insulation drying for 2 hours or 600oF.
Flux particle size
Taylor's mesh: 10 times 100
packaging
The barrel cover is covered with a 60 - pound polyethylene barrel sealed with rubber gasketINCOFLUXR 4 埋弧焊劑與INCONEL 82焊絲匹配INCOFLUXR 4 埋弧焊劑與INCONEL 82焊絲匹配INCOFLUXR 4 埋弧焊劑與INCONEL 82焊絲匹配INCOFLUXR 4 埋弧焊劑與INCONEL 82焊絲匹配INCOFLUXR 4 埋弧焊劑與INCONEL 82焊絲匹配