不銹鋼 焊條 |
308L/MVR |
E308L-17 |
0.02 |
0.8 |
1.0 |
20.0 |
10.5 |
|
|
308L/MVR |
E308L-15 |
0.03 |
0.2 |
1.7 |
20.0 |
10.0 |
|
|
|
308L/MVR |
E308L-16 |
0.03 |
0.3 |
1.5 |
20.0 |
10.0 |
|
|
|
308/308H |
E308H-17 |
0.06 |
0.7 |
1.1 |
20.0 |
10.0 |
|
|
|
347/MVNb |
E347-17 |
0.02 |
0.8 |
0.8 |
19.5 |
10.0 |
|
|
|
347/MVNb |
E347-15 |
0.06 |
0.2 |
1.7 |
19.5 |
10.0 |
|
|
|
316L/SKR |
E316L-17 |
0.02 |
0.8 |
1.1 |
18.5 |
12.0 |
2.8 |
|
|
316L/SKR |
E316L-15 |
0.03 |
0.2 |
1.7 |
18.5 |
12.0 |
2.8 |
|
|
316L/SKR |
E316L-16 |
0.02 |
0.3 |
1.4 |
19.0 |
12.0 |
2.8 |
|
|
316/316H |
E316H-17 |
0.06 |
0.8 |
1.0 |
19.0 |
12.0 |
2.8 |
|
|
318/SKNb |
E318-17 |
0.02 |
0.8 |
0.8 |
18.5 |
12.0 |
2.8 |
|
|
318/SKNb |
E318-15 |
0.04 |
0.2 |
2.1 |
18.5 |
12.5 |
2.7 |
|
|
317L/SNR |
E317L-17 |
0.02 |
0.7 |
0.9 |
19.0 |
13.0 |
3.7 |
|
|
2205 |
E2209-17 |
0.02 |
0.8 |
0.7 |
23.0 |
9.5 |
3.0 |
|
|
2205 |
E2209-15 |
0.02 |
0.5 |
0.8 |
23.0 |
9.5 |
3.0 |
|
|
904L |
E385-17 |
0.02 |
0.8 |
1.2 |
20.5 |
25.0 |
4.5 |
|
|
383 |
E383-17 |
0.02 |
0.9 |
0.9 |
27.0 |
32.0 |
3.7 |
|
|
P12-R |
EniCrMo-12 |
0.02 |
0.4 |
0.4 |
21.5 |
|
9.5 |
|
|
P625 |
EniCrMo-3 |
0.02 |
0.5 |
0.2 |
21.5 |
|
9.5 |
|
|
307 |
E307-17 |
0.07 |
0.8 |
4.0 |
20.0 |
10.5 |
0.8 |
|
|
309L |
E309L-15 |
0.03 |
0.2 |
1.9 |
24.0 |
13.0 |
|
|
|
P5 |
E309MoL-17 |
0.02 |
0.8 |
1.1 |
22.5 |
13.5 |
2.7 |
|
|
P5 |
E309MoL-15 |
0.03 |
0.2 |
2.0 |
22.5 |
13.0 |
2.7 |
|
|
P5 |
E309MoL-16 |
0.03 |
0.3 |
1.4 |
22.5 |
13.5 |
2.7 |
|
|
P7 |
E312-17 |
0.09 |
0.8 |
0.8 |
29.0 |
9.5 |
|
|
|
P10 |
ENiCrFe-3 |
0.02 |
0.4 |
6.5 |
16.0 |
|
|
|
|
309 |
E309-17 |
0.05 |
0.8 |
1.0 |
24.0 |
13.5 |
|
|
|
310 |
E310-17 |
0.10 |
0.5 |
2.1 |
26.0 |
21.0 |
|
|
|
310 |
E310-15 |
0.12 |
0.3 |
2.4 |
25.5 |
21.0 |
|
|
焊條 |
BOHLER FOX CEL |
E6010 |
0.12 |
0.14 |
0.5% |
|
|
450 |
520 |
26 |
用于垂直下向焊接直流負(fù)極的根焊再接直流正極的熱焊、填充、蓋面焊 |
|
BOHLER FOX CEL+ |
E6010 |
0.15 |
0.15 |
0.6% |
|
|
450 |
520 |
26 |
除具有優(yōu)良的焊接和過濾性外，同時(shí)在防止縮孔和咬邊焊接缺陷方面也有很高的安全性 |
|
|
BOHLER FOX CELMo |
E7010-a1 |
0.10 |
0.14 |
0.4% |
0.5% |
|
480 |
550 |
23 |
適用于垂直下向的熱焊和填充焊，也適用于APE X56/X60或L385M/L415MB |
|
|
BOHLER FOX CEL75 |
E7010-P1 |
0.14 |
0.14 |
0.7% |
|
|
480 |
550 |
23 |
尤其適用于鋼種為X56和X60或L385M/L415MB的管材 |
|
|
BOHLER FOX CEL85 |
E8010-P1 |
0．14 |
0．10 |
0．7 |
|
0．6% |
490 |
570 |
23 |
是最常用且適應(yīng)性強(qiáng)纖維素焊條，它能極其充分地滿足橫貫國家的管道實(shí)地焊接的各種嚴(yán)格的要求 |
|
|
BOHLER FOX CEL90 |
E9010-G |
0.17 |
0.15 |
0.9 |
|
0.8% |
610 |
650 |
21 |
保證焊縫熔敷金屬的優(yōu)良機(jī)械性能、最高金相質(zhì)量和可靠性 |
|
|
BOHLER FOX BVD RP |
E8018-G |
0.05 |
0.3 |
1.0% |
|
|
510 |
560 |
26 |
根部焊道垂直下向焊接用的堿性藥皮焊條 |
|
|
HLER FOX BVD 85 |
E8018-G |
0.04 |
0.4 |
0.9 |
|
0.9% |
510 |
560 |
27 |
產(chǎn)生起始密集氣孔 |
|
|
BOHLER FOX BVD 90 |
E9018-G |
0.04 |
0.3 |
1.2 |
|
2.2% |
600 |
650 |
27 |
防止氫誘導(dǎo)的焊縫冷開裂的高度安全性，應(yīng)用于管壁厚度達(dá)到36.2mm |
|
|
BOHLER FOX BVD 100 |
E10018-G |
0.07 |
0.4 |
1.2 |
|
2.3% |
670 |
730 |
24 |
特殊的起弧特性，并避免蓋面焊道產(chǎn)生起始密集氣孔，填充焊道的各項(xiàng)要求 |
|
|
FOX BVD 110 |
E11018-G |
0.07 |
0.4 |
1.2 |
0.3% |
2.0 |
720 |
810 |
20 |
易于操作，低氫含量和垂直下向焊接的低熱量輸入進(jìn)一步有利于細(xì)晶粒高抗拉強(qiáng)度鋼種管道接頭的經(jīng)濟(jì)焊接 |
|
|
BOHELR FOX EV PIPE |
E7016-1H4R |
0.06 |
0.60 |
0.9 |
|
0.17% |
470 |
560 |
29 |
垂直上向焊低氫焊條，它易于操作且能充分滿足焊工需要 |