| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動速率 | 200℃/5kg | ASTM D-1238 | 7 | g/10min |
| 物理性能 | 比重 | ASTM D-792 | 1.04 | g/cm3 | |
| 模具收縮率 | ASTM D-955 | 0.004-0.007 | cm/cm | ||
| 機械性能 | 拉伸屈服強度 | ASTM D-638 | 48 | MPa | |
| 拉伸斷裂強度 | ASTM D-638 | 48 | MPa | ||
| 斷裂伸長率 | ASTM D-638 | 2 | % | ||
| 彎曲強度 | ASTM D-790 | 90 | MPa | ||
| 彎曲模量 | ASTM D-790 | 3241 | MPa | ||
| IZOD缺口沖擊強度 | 23℃ | ASTM D-256 | 16 | J/m | |
| 熱性能 | 線性膨脹系數(shù) | 10-5 | 7.6 | cm/cm/℃ | |
| 阻燃等級 | 1.5mm | UL 94 | HB | ||
| 維卡軟化點 | ASTM D-1525 | 99 | ℃ | ||
| 熱變形溫度 | 1.82MPa，未經(jīng)退火 | ASTM D-648 | 76 | ℃ | |
| 熱變形溫度 | 1.82MPa，經(jīng)退火 | ASTM D-648 | 94 | ℃ | |