產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 2.6 | g/10min |
| 熔體流動速率 | 190℃/2.16kg | ISO 1133 | 2.6 | g/10min | |
| 單體含量 | Internal Method | 6.5 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.935 | g/cm3 | |
| 比重 | ISO 1183/A | 0.935 | g/cm3 | ||
| 機械性能 | 拉伸屈服強度 | Compression Molded | ASTM D-638 | 10 | MPa |
| 拉伸屈服強度 | Compression Molded | ISO 527-2/508 | 10 | MPa | |
| 拉伸斷裂強度 | Compression Molded | ASTM D-638 | 20.1 | MPa | |
| 拉伸斷裂強度 | Compression Molded | ISO 527-2/508 | 20.1 | MPa | |
| 拉伸斷裂伸長率 | Compression Molded | ASTM D-638 | 640 | % | |
| 拉伸斷裂伸長率 | Compression Molded | ISO 527-2/508 | 640 | % | |
| 薄膜厚度-Tested | 50.8 | um | |||
| 拉伸屈服強度 | 50.8um | ASTM D-882 | TDMD11.111.3 | MPa | |
| 拉伸屈服強度 | 50.8um | ISO 527-3 | TDMD11.511.3 | MPa | |
| 拉伸斷裂強度 | 50.8um | ASTM D-882 | TDMD31.831.8 | MPa | |
| 拉伸斷裂強度 | 50.8um | ISO 527-3 | TDMD31.831.8 | MPa | |
| 拉伸斷裂伸長率 | 50.8um | ASTM D-882 | MDTD460510 | % | |
| 拉伸斷裂伸長率 | 50.8um | ISO 527-3 | MDTD460510 | % | |
| 落錘沖擊 | 50.8um | ASTM D-1709B | 410 | g | |
| 落錘沖擊 | 50.8um | ISO 7765-1/B | 410 | g | |
| 埃爾曼多夫撕裂強度 | 50.8um | ASTM D-1922 | MDTD270390 | g | |
| 埃爾曼多夫撕裂強度 | 50.8um | ISO 6383-2 | MDTD12001700 | N | |
| 加工性能 | 熔體溫度 | 193 | ℃ | ||
| 熱性能 | 維卡軟化點 | ASTM D-1525 | 88.9 | ℃ | |
| 維卡軟化點 | ISO 306 | 88.9 | ℃ | ||
| 熔化溫度 | DSC | 103 | ℃ | ||
| 光學性能 | 光澤度 | 45°，50.8um | ASTM D-2457 | 76 | |
| 霧度 | 50.8um | ASTM D-1003 | 3.7 | % | |
| 霧度 | 50.8um | ISO 14782 | 3.7 | % | |