| 密度 | 1.70 | g/cm3 | ASTM D792 |
| 成型收縮率 | |||
| (流動(dòng)) | 0.18 | % | |
| (橫向流動(dòng)) | 1.2 | % | |
| 吸水率 | 0.020 | % | ASTM D570 |
| 洛氏硬度 | 103 | ASTM D785 |
| 抗張強(qiáng)度 | 147 | MPa | ASTM D638 |
| 斷裂伸長(zhǎng)率 | 5.2 | % | ASTM D638 |
| 彎曲模量 (23℃) | 12300 | MPa | ASTM D790 |
| 彎曲強(qiáng)度 (23℃.屈服) | 143 | MPa | ASTM D790 |
| 剪切強(qiáng)度 | 51.0 | MPa | ASTM D732 |
| 泊松比 | 0.46 | ASTM E132 | |
| 懸臂梁缺口沖擊強(qiáng)度 (6.4mm) | 110 | J/m | ASTM D256 |
| 無(wú)缺口懸臂梁沖擊強(qiáng)度 (6.4mm) | 410 | J/m | ASTM D256 |
| 熱變形溫度 (1.8MPa) | 279 | ℃ | ASTM D648 |
| 導(dǎo)熱率 | 0.52 | W/m/K | JIS R2618 |
| 阻燃性 | V-0 | UL 94 | |
| 極限氧指數(shù) | 48 | % | JIS K7201 |
| 體積電阻率 | 1.0E+15 | ohm.cm | ASTM D257 |
| 介電常數(shù) | ASTM D150 | ||
| (1kHz) | 4.50 | ||
| (1MHz) | 3.90 | ||
| 介電因子 | ASTM D150 | ||
| (1kHz) | 0.022 | ||
| (1MHz) | 0.032 | ||
| 耐電弧性 | 130 | sec | ASTM D495 |
| 漏電起痕指數(shù) | 125 | V | IEC 60112 |