| 密度 | 1080 | kg/m | ISO 1183 |
| 吸水率 (equilibrium in water at 23°C) | 0.7 | % | similar to ISO 62 |
| 熔體體積流動速率 | 17 | cm/10min | ISO 1133 |
| 模具收縮率 | 0.4-0.7 | % |
| 拉伸模量 | 2000 | MPa | ISO 527-1/-2 |
| 屈服應力 (50mm/min) | 48 | MPa | ISO 527-1/-2 |
| 屈服應變 (50mm/min) | 4 | % | ISO 527-1/-2 |
| 斷裂應變 (50mm/min) | 12 | % | ISO 527-1/-2 |
| Charpy無缺口沖擊強度 | ISO 179/1eU | ||
| (+23℃) | 180 | KJ/m | |
| (-30℃) | 120 | KJ/m | |
| CHARPY缺口沖擊強度 | ISO 179/1eA | ||
| (+23℃) | 10 | KJ/m | |
| (-30℃) | 2 | KJ/m | |
| 球壓痕硬度 | 70 | MPa | ISO 2039-1 |
| 介電常數(shù) | IEC 60250 | ||
| (100Hz) | 2.9 | ||
| (1MHz) | 2.8 | ||
| 介質損耗因數(shù) | IEC 60250 | ||
| (100Hz) | 160 | E-4 | |
| (1MHz) | 140 | E-4 | |
| 體積電阻率 (100V) | 1E13 | Ohm*m | IEC 60093 |
| 表面電阻率 (100V) | 1E15 | Ohm | IEC 60093 |
| 介電強度 | 34 | KV/mm | IEC 60243-1 |
| 熱變形溫度 | ISO 75-1/-2 | ||
| (1.80MPa) | 90 | ℃ | |
| (0.45MPa) | 94 | ℃ | |
| 維卡軟化溫度 | ISO 306 | ||
| (VST/A/50) | 105 | ℃ | |
| (VST/B/50) | 93 | ℃ |