產(chǎn)品參數(shù)
| 吸水率 (23℃) | 1.3 | % | ASTM D-570 |
| 模具收縮率 (23℃) | 1.5-2.0 | % | ASTM D-955 |
| 比重 (23℃) | 1.14 | ISO 1183 |
| 斷裂伸長率 (77℃) | 30 | % | ASTM D-638 |
| 彎曲強(qiáng)度 (23℃) | 90 | MPa | ASTM D-790 |
| 拉伸模量 (23℃) | 2960 | MPa | ASTM D-638 |
| 拉伸強(qiáng)度 (23℃) | 83 | MPa | ISO 527 |
| 斷裂伸長率 (-40℃) | 5 | % | ASTM D-638 |
| IZOD沖擊強(qiáng)度 (-40℃) | 2.2 | KJ/m | ISO 180 |
| 斷裂伸長率 (23℃) | 10 | % | ASTM D-638 |
| 彎曲模量 (23℃) | 2860 | MPa | ISO 178 |
| IZOD沖擊強(qiáng)度 (23℃) | 6 | KJ/m | ISO 180 |
| 介電常數(shù) (23℃) | 3.7 | ASTM D-150 | |
| 損耗因素 (10Hz.23℃) | 0.03 | ASTM D-150 | |
| 介電強(qiáng)度 | ASTM D-149 | ||
| (23℃.short time) | 22 | kv/mm | |
| (23℃.step-by-step) | 22 | kv/mm | |
| 介電常數(shù) (10Hz.23℃) | 3.6 | ASTM D-150 | |
| 損耗因素 (10Hz.23℃) | 0.02 | ASTM D-150 | |
| 體積電阻率 (23℃) | 6.0×10 | Ω.cm | ASTM D-257 |
| 損耗因素 (10Hz.23℃) | 0.02 | ASTM D-150 | |
| 介電常數(shù) (10Hz.23℃) | 3.1 | ASTM D-150 |
| 熔點(diǎn) | 260 | ℃ | ISO 3146 |
| 熱變形溫度 (1.80MPa) | 64 | ℃ | ISO 75 |