| 比重 | 1.58 | g/cm3 | No Standard |
| 熔流率 (320℃/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| 收縮率 (流動: 1.00 mm) | 0.10 | % | No Standard |
| (橫向流動: 1.00 mm) | 0.60 | % | No Standard |
| 吸水率 (飽和, 40℃) | 1.0 | % | No Standard |
| 抗張強度 | 190 | MPa | ASTM D638 |
| 伸長率 (斷裂) | 4.3 | % | ASTM D638 |
| 彎曲模量 | 10000 | MPa | ASTM D790 |
| 彎曲強度 | 240 | MPa | ASTM D790 |
| 懸壁梁缺口沖擊強度 | 100 | J/m | ASTM D256 |
| 熱變形溫度 (1.8 MPa, 未退火) | 285 | ℃ | ASTM D648 |
| 玻璃轉(zhuǎn)化溫度 (DSC) | 125 | ℃ | No Standard |
| 熔融溫度 | 306 | ℃ |
| 體積電阻率 | 1.0E+16 | ohm·cm | ASTM D257 |
| 介電強度 | 30 | kV/mm | ASTM D149 |
| 相對電容率 (10.0 GHz) | 3.40 | ASTM D150 | |
| 耗散因數(shù) (10.0 GHz) | 0.010 | ASTM D150 | |
| 相比耐漏電起痕指數(shù) (CTI) | PLC 1 | UL 746 |
| UL 阻燃等級 | V-0 | UL 94 |