| 密度 | 1.13 | g/cm | ISO 1183 |
| 成型收縮率 | 0.009 | in/in | ASTM D955 |
| 吸水率 | |||
| (24hrs) | 1.6 | % | ASTM D570 |
| (24h/23C) | 1.6 | % | ISO 62 |
| (73℉) | 9.3 | % | ASTM D570 |
| (23C) | 9.3 | % | ISO 62 |
| (23C/50RH) | 2.6 | % | ISO 62 |
| 吸濕率 | 2.6 | % | ISO 62 |
| 硬度 | 120 | ASTM D785 |
| 拉伸模量 | ISO 527-1,-2 | ||
| (-40℉) | 593000 | psi | |
| (176℉) | 109000 | psi | |
| (248℉) | 79800 | psi | |
| 537000 | psi | ||
| 拉伸屈服強(qiáng)度 | ASTM D638 | ||
| (-40℉) | 19900 | psi | |
| (248℉) | 4350 | psi | |
| 拉伸屈服應(yīng)力 | ISO 527-1,-2 | ||
| (-40℉) | 19900 | psi | |
| (176℉) | 5800 | psi | |
| (248℉) | 4350 | psi | |
| 屈服應(yīng)力 | 12800 | psi | ISO 527-1,-2 |
| 斷裂拉伸強(qiáng)度 | ASTM D638 | ||
| (-40℉) | 18900 | psi | |
| (176℉) | 5080 | psi | |
| (248℉) | 3630 | psi | |
| 斷裂拉伸應(yīng)力 (-40℉) | 18900 | psi | ISO 527-1,-2 |
| 屈服伸長率 | ASTM D638 | ||
| (-40℉) | 3.0 | % | |
| (176℉) | 25 | % | |
| (248℉) | 27 | % | |
| 屈服應(yīng)變 | 4.0 | % | ISO 527-1,-2 |
| 斷裂伸長率 | ASTM D638 | ||
| (-40℉) | 5.0 | % | |
| (176℉) | 100 | % | |
| (248℉) | 100 | % | |
| 彎曲模量 | ASTM D790 | ||
| (-40℉) | 489000 | psi | |
| (73℉) | 460000 | psi | |
| (149℉) | 87000 | psi | |
| (199℉) | 63800 | psi | |
| (248℉) | 55800 | psi | |
| (73℉) | 406000 | psi | |
| 彎曲強(qiáng)度 | ASTM D790 | ||
| (-40℉) | 26500 | psi | |
| (73℉) | 16000 | psi | |
| (149℉) | 4350 | psi | |
| (248℉) | 3050 | psi | |
| (73℉) | 13800 | psi | |
| CHARPY缺口沖擊強(qiáng)度 (23℃) | 1.67 | ft·lb/in | ISO 179/1eA |
| IZOD缺口沖擊 | ASTM D256 | ||
| (-40℉) | 0.599 | ft·lb/in | |
| (73℉) | 0.899 | ft·lb/in |
| 表面電阻系數(shù) | ＞3.9E+12 | ohm·in | IEC 60093 |
| 熔點(diǎn) | 428 | ℉ | |
| 阻燃性 | V-2 | ISO 1210 |