| 吸水率 (24小時 23℃) | 1.3 | % | ASTM D-570 |
| 比重 | 1.25 | ASTM D-792 |
| 強化含量 | 15 | WT% | |
| 抗燃級 | HB | 1/16") | UL94 |
| 泰伯磨耗量 ((1000g,CS-17)23℃) | 10 | mg/1000次 | ASTM D-1044 |
| 壓縮強度 (80℃) | 700 | kg/cm | ASTM D-695 |
| 抗拉屈股強度 (-40℃) | 1400 | kg/cm | ASTM D-638 |
| 撓曲模量 (23℃) | 51000 | kg/cm | ASTM D-790 |
| 埃佐德衡擊 (23℃ 無缺口1/8) | 30 | kg·cm/cm | |
| 撓曲模量 (80℃) | 21000 | kg/cm | ASTM D-790 |
| 裂斷伸長率 | ASTM D-638 | ||
| (80℃) | 9 | % | |
| (-40℃) | 3.5 | % | |
| 埃佐德衡擊 (23℃ V-缺口1/2) | 5 | kg·cm/cm | ASTM D-256 |
| 撓曲強度 (80℃) | 700 | kg/cm | ASTM D-790 |
| 埃佐德衡擊 (-40℃ V-缺口1/2) | 4.5 | kg·cm/cm | ASTM D-256 |
| 洛氏硬度 (M-標度 23℃) | 90 | ASTM D-785 | |
| 撓曲模量 (-40℃) | 68000 | kg/cm | ASTM D-790 |
| 壓縮強度 (-40℃) | 2050 | kg/cm | ASTM D-695 |
| 埃佐德衡擊 (-40℃ 無缺口1/8) | 19 | kg·cm/cm | |
| 抗拉屈股強度 | ASTM D-638 | ||
| (23℃) | 1050 | kg/cm | |
| (80℃) | 450 | kg/cm | |
| 裂斷伸長率 (23℃) | 4 | % | ASTM D-638 |
| 洛氏硬度 (R-標度 23℃) | 119 | ASTM D-785 | |
| 撓曲強度 | ASTM D-790 | ||
| (-40℃) | 1800 | kg/cm | |
| (23℃) | 1500 | kg/cm | |
| 壓縮強度 (23℃) | 1400 | kg/cm | ASTM D-695 |
| 體積電阻率 | 10 | Ω·cm | ASTM D-257 |
| 介電強度 (短時間 1/8") | 20 | KV/mm | ASTM D-149 |
| 熱撓曲溫度 | ASTM D-648 | ||
| (18.6kg/cm) | 175 | ℃ | |
| (4.6kg/cm) | 210 | ℃ | |
| 線性熱膨脹系數(shù) | 4.5 | ×10-5cm/cm/℃ | ASTM D-696 |
| 熔點 | 225 | ℃ | 差示掃描測熱計DSC |
| 比熱 | 0.37 | Cal/g·℃ |