| 吸水率 (23℃.24小時(shí)) | 無水|3%水1.3|- | % | ASTM D-570 |
| 泰伯磨耗量 ((1000g,CS-17)23℃) | 無水|3%水10|- | mg/1000次 | ASTM D-1044 |
| 比重 | 無水|3%水1.25|- | ASTM D-792 |
| 抗剪強(qiáng)度 (80℃) | 無水|3%水-|770 | Kg/cm | ASTM D-732 |
| IZOD沖擊強(qiáng)度 (V-缺口1/2.23℃) | 無水|3%水6|28 | kg·cm/cm | ASTM D-256 |
| 抗拉屈服強(qiáng)度 (23℃) | 無水|3%水1200|5300 | Kg/cm | ASTM D-638 |
| 抗剪強(qiáng)度 (23℃) | 無水|3%水-|770 | Kg/cm | ASTM D-732 |
| 斷裂伸長(zhǎng)率 (23℃) | 無水|3%水4|<200 | % | ASTM D-638 |
| 撓曲模量 (-40℃) | 無水|3%水68000|42000 | Kg/cm | ASTM D-790 |
| 洛氏硬度 | ASTM D-785 | ||
| (23℃) | 無水|3%水90|100 | M-標(biāo)度 | |
| (23℃) | 無水|3%水119|100 | R-標(biāo)度 | |
| 抗拉斷裂強(qiáng)度 (23℃) | 無水|3%水-|730 | Kg/cm | ASTM D-638 |
| 斷裂伸長(zhǎng)率 | ASTM D-638 | ||
| (-40℃) | 無水|3%水3.5|<200 | % | |
| (80℃) | 無水|3%水10|<200 | % | |
| 撓曲強(qiáng)度 | ASTM D-790 | ||
| (80℃) | 無水|3%水850|400 | Kg/cm | |
| (23℃) | 無水|3%水1700|650 | Kg/cm | |
| (-40℃) | 無水|3%水2100|1300 | Kg/cm | |
| 抗拉屈服強(qiáng)度 | ASTM D-638 | ||
| (-40℃) | 無水|3%水1550|1100 | Kg/cm | |
| (80℃) | 無水|3%水550|400 | Kg/cm | |
| 撓曲模量 | ASTM D-790 | ||
| (23℃) | 無水|3%水51000|14000 | Kg/cm | |
| (80℃) | 無水|3%水21000|5000 | Kg/cm |
| 介電強(qiáng)度 (1/8") | 無水|3%水20|- | KV/mm | ASTM D-149 |
| 體積電阻率 | 無水|3%水 10|10-10 | Ω.cm | ASTM D-257 |
| 熱撓曲溫度 (18.6kg/cm) | 無水|3%水175|- | ℃ | ASTM D-648 |
| 比熱 | 無水|3%水0.37|- | Cal/g·℃ | |
| 線性熱膨脹系數(shù) | 無水|3%水4.5|- | ×10-5cm/cm/℃ | ASTM D-696 |
| 熱撓曲溫度 (4.6kg/cm) | 無水|3%水210|- | ℃ | ASTM D-648 |
| 熔點(diǎn) | 無水|3%水225|- | ℃ | 差示掃描測(cè)熱計(jì)DSC |
| 強(qiáng)化含量 | 無水|3%水15|- | WT% |