| 吸水率 (23℃.24小時(shí)) | 無水|3.5%水1.8|- | % | ASTM D-570 |
| 比重 | 無水|3.5%水1.12-1.14|- | ASTM D-792 | |
| 泰伯磨耗量 (1000g,CS-17) | 無水|3.5%水3-4|- | mg/1000次 | ASTM D-1044 |
| 抗拉屈服強(qiáng)度 (-40℃) | 無水|3.5%水1130|1000 | Kg/cm | ASTM D-638 |
| 撓曲模量 (23℃) | 無水|3.5%水25000|8000 | Kg/cm | ASTM D-790 |
| 撓曲強(qiáng)度 | ASTM D-790 | ||
| (-40℃) | 無水|3.5%水1400|1300 | Kg/cm | |
| (80℃) | 無水|3.5%水430|250 | Kg/cm | |
| (23℃) | 無水|3.5%水1000|400 | Kg/cm | |
| 壓縮強(qiáng)度 (23℃) | 無水|3.5%水840|- | Kg/cm | ASTM D-695 |
| 斷裂伸長率 (23℃) | 無水|3.5%水130|< 200 | % | ASTM D-638 |
| 撓曲模量 | ASTM D-790 | ||
| (80℃) | 無水|3.5%水7000|3000 | Kg/cm | |
| (-40℃) | 無水|3.5%水39000|37000 | Kg/cm | |
| 洛氏硬度 (23℃) | 無水|3.5%水119|88 | R-標(biāo)度 | ASTM D-785 |
| 抗拉屈服強(qiáng)度 (80℃) | 無水|3.5%水270|200 | Kg/cm | ASTM D-638 |
| 抗拉斷裂強(qiáng)度 (23℃) | 無水|3.5%水700|- | Kg/cm | |
| 洛氏硬度 (80℃) | 無水|3.5%水80|- | R-標(biāo)度 | ASTM D-785 |
| 抗拉屈服強(qiáng)度 (23℃) | 無水|3.5%水760|350 | Kg/cm | ASTM D-638 |
| IZOD沖擊強(qiáng)度 (V-缺口1/2.23℃) | 無水|3.5%水5|40 | kg.cm/cm | |
| 抗剪強(qiáng)度 (23℃) | 無水|3.5%水720|650 | Kg/cm | ASTM D-732 |
| 抗電弧性 (1/8) | 無水|3.5%水121|- | 秒 | ASTM D-495 |
| 介電常數(shù) (10Hz) | 無水|3.5%水3.9|- | ASTM D-150 | |
| 損耗因數(shù) (10Hz) | 無水|3.5%水0.03|- | ASTM D-150 | |
| IEC導(dǎo)電徑跡指數(shù) | 無水|3.5%水≤600|- | V | UL 746 |
| 體積電阻率 | 無水|3.5%水 10-10|10-10 | Ω.cm | ASTM D-257 |
| 損耗因數(shù) (10Hz) | 無水|3.5%水0.06|- | ASTM D-150 | |
| 介電常數(shù) | ASTM D-150 | ||
| (10Hz) | 無水|3.5%水3.4|- | ||
| (50Hz) | 無水|3.5%水4.1|- | ||
| 介電強(qiáng)度 (1/8) | 無水|3.5%水20|- | KV/mm | ASTM D-149 |
| 損耗因數(shù) (50Hz) | 無水|3.5%水0.07|- | ASTM D-150 |
| 導(dǎo)熱系數(shù) | 無水|3.5%水0.18|- | Kcal/m·hr·℃ | |
| 熱撓曲溫度 (4.6kg/cm) | 無水|3.5%水182|- | ℃ | ASTM D-695 |
| 線性熱膨脹系數(shù) | ASTM D-696 | ||
| 無水|3.5%水0.18|- | ×10-5cm/cm/℃ | ||
| 無水|3.5%水8|- | ×10-5cm/cm/℃ | ||
| 熔點(diǎn) | 無水|3.5%水225|- | ℃ | 差示掃描測熱計(jì)DSC |
| UL-94抗燃級 | 無水|3.5%水V-2(1/32")|- | UL 94 | |
| 比熱 | 無水|3.5%水0.46|- | Cal/g·℃ |