| 吸水率 | ASTM D-570 | ||
| (23℃.24hr) | Dry|1.9%Water0.9|- | % | |
| (23℃) | Dry|1.9%Water5.3|- | % |
| 比重 | Dry|1.9%Water1.50|- | ASTM D-792 |
| 斷裂伸長(zhǎng)率 (-40℃) | Dry|1.9%Water4.5|4.5 | % | ASTM D-638 |
| 彎曲模量 (23℃) | Dry|1.9%Water12.0|7.1 | GPa | ASTM D-790 |
| IZOD缺口沖擊強(qiáng)度 (-40℃) | Dry|1.9%Water125|145 | J/m | ASTM D-256 |
| 彎曲模量 (80℃) | Dry|1.9%Water6.2|4.4 | GPa | ASTM D-790 |
| 拉伸屈服強(qiáng)度 (23℃) | Dry|1.9%Water205|130 | MPa | ASTM D-638 |
| 彎曲模量 (-40℃) | Dry|1.9%Water14.0|12.5 | GPa | ASTM D-790 |
| 彎曲強(qiáng)度 (23℃) | Dry|1.9%Water290|180 | MPa | ASTM D-790 |
| 斷裂伸長(zhǎng)率 (23℃) | Dry|1.9%Water5.0|5.0 | % | ASTM D-638 |
| 拉伸屈服強(qiáng)度 (80℃) | Dry|1.9%Water120|85 | MPa | ASTM D-638 |
| IZOD無(wú)缺口沖擊強(qiáng)度 (23℃) | Dry|1.9%Water100|120 | KJ/m | ASTM D-256 |
| 彎曲強(qiáng)度 (-40℃) | Dry|1.9%Water330|280 | MPa | ASTM D-790 |
| IZOD缺口沖擊強(qiáng)度 (23℃) | Dry|1.9%Water155|195 | J/m | ASTM D-256 |
| 抗壓強(qiáng)度 | ASTM D-695 | ||
| (-40℃) | Dry|1.9%Water260|220 | MPa | |
| (23℃) | Dry|1.9%Water190|120 | MPa | |
| (80℃) | Dry|1.9%Water100|70 | MPa | |
| 剪切強(qiáng)度 (23℃) | Dry|1.9%Water95|75 | MPa | ASTM D-732 |
| 斷裂伸長(zhǎng)率 (80℃) | Dry|1.9%Water8.0|8.0 | % | ASTM D-638 |
| 彎曲強(qiáng)度 (80℃) | Dry|1.9%Water160|110 | MPa | ASTM D-790 |
| 洛氏硬度 (23℃) | Dry|1.9%WaterR121,M95|- | R Scale | ASTM D-785 |
| IZOD無(wú)缺口沖擊強(qiáng)度 (-40℃) | Dry|1.9%Water90|95 | KJ/m | ASTM D-256 |
| 拉伸屈服強(qiáng)度 (-40℃) | Dry|1.9%Water290|250 | MPa | ASTM D-638 |
| 熱導(dǎo)率 | Dry|1.9%Water0.40|- | W/m℃ | |
| 線性熱膨脹系數(shù) | Dry|1.9%Water2-3|- | 10-5/℃ | ASTM D-696 |
| 比熱 | Dry|1.9%Water1.4|- | J/p℃ | |
| 熔點(diǎn) | Dry|1.9%Water225|- | ℃ | DSC |
| 熱變形溫度 | ASTM D-648 | ||
| (0.46MPa) | Dry|1.9%Water225|- | ℃ | |
| (1.86MPa) | Dry|1.9%Water215|- | ℃ |
| 加強(qiáng)材料 | Dry|1.9%Water45|45 | WT% |