| 填充含量 | 15 | Wt% | |
| 比重 | 1.47 | D792 | |
| 吸水率 | D570 | ||
| (23℃,24hrs) | 0.4 | % | |
| (23℃,水中) | 5.0 | % | |
| 洛氏硬度 (23℃) | 120 | R | D785 |
| 拉伸屈服強(qiáng)度 | D638 | ||
| (-40℃) | 145 | MPa | |
| (23℃) | 125 | MPa | |
| (80℃) | 60 | MPa | |
| - (23℃) | 5 | % | D638 |
| 彎曲強(qiáng)度 | D790 | ||
| (23℃) | 190 | MPa | |
| (80℃) | 120 | MPa | |
| 彎曲模量 | D790 | ||
| (23℃) | 5.7 | Gpa | |
| (80℃) | 3.2 | Gpa | |
| 沖擊強(qiáng)度 | D256 | ||
| (23℃) | 40 | J/M | |
| (23℃) | 50 | KJ/m | |
| 磨耗 | 12 | mg/1000 | D1044 |
| 體積電阻率 | 10 | Ω.m | D257 |
| 縮模率 | |||
| (1mmt) | 0.4-0.6 | % | |
| (3mmt) | 0.8-1.2 | % |
| 熔點(diǎn) | 265 | ℃ | DSC |
| 熱變形溫度 (1.86MPa) | 244 | ℃ | D648 |
| 阻燃性 | V-0 | UL94 |