| 密度 | 1.43 g/cc | 0.0517 lb/in3 | Crystalline; ISO 1183 |
| Water Absorption at Saturation | 0.40 % @Temperature 23.0 °C | 0.40 % @Temperature 73.4 °F | E; by immersion; ISO 62-1 |
| 0.45 % @Temperature 100 °C | 0.45 % @Temperature 212 °F | immersion; ISO 62-1 | |
| 粘度 | 475000 cP @Temperature 400 °C | 475000 cP @Temperature 752 °F | melt; ISO 11443 |
| 線性成型收縮率,Flow | 0.0030 cm/cm | 0.0030 in/in | 360°C nozzle, 160°C tool; ISO 294-4 |
| 線性成型收縮率，橫向 | 0.0090 cm/cm | 0.0090 in/in | 380°C nozzle, 190°C tool; ISO 294-4 |
| Spiral Flow | 10.0 cm @Thickness 1.00 mm | 3.94 in @Thickness 0.0394 in | 380°C nozzle, 190°C tool |
| 抗張強度(斷裂) | 160 MPa @Temperature 23.0 °C | 23200 psi @Temperature 73.4 °F | ISO 527 |
| 伸長率 (斷裂) | 3.4 % @Temperature 23.0 °C | 3.4 % @Temperature 73.4 °F | ISO 527 |
| 拉伸模量 | 8.80 GPa @Temperature 23.0 °C | 1280 ksi @Temperature 73.4 °F | ISO 527 |
| 彎曲強度 | 250 MPa @Temperature 23.0 °C | 36300 psi @Temperature 73.4 °F | ISO 178 |
| 彎曲模量 | 8.30 GPa @Temperature 23.0 °C | 1200 ksi @Temperature 73.4 °F | ISO 178 |
| 懸壁梁缺口沖擊強度 | 10.0 kJ/m2 @Temperature 23.0 °C | 4.76 ft-lb/in2 @Temperature 73.4 °F | ISO 180/A |
| 懸壁梁無缺口沖擊強度 | 65.0 kJ/m2 @Temperature 23.0 °C | 30.9 ft-lb/in2 @Temperature 73.4 °F | ISO 180/U |
| 體積電阻率 | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | IEC 60093 |
| 介電常數(shù) | 3.1 @Frequency 1000 Hz, Temperature 23.0 °C | 3.1 @Frequency 1000 Hz, Temperature 73.4 °F | IEC 60250 |
| 介電強度 | 24.0 kV/mm @Thickness 2.00 mm | 610 kV/in @Thickness 0.0787 in | IEC 60243-1 |
| 耗散因數(shù) | 0.0050 @Frequency 1.00e+6 Hz, Temperature 23.0 °C | 0.0050 @Frequency 1.00e+6 Hz, Temperature 73.4 °F | IEC 60250 |
| 相比耐漏電起痕指數(shù)(CTI) | 150 V | 150 V | IEC 60112 |
| 線性熱膨脹系數(shù) | 45.0 μm/m-°C @Temperature <=143 °C | 25.0 μin/in-°F @Temperature <=289 °F | Average below Tg; ISO 11359 |
| 120 μm/m-°C @Temperature >=143 °C | 66.7 μin/in-°F @Temperature >=289 °F | Average above Tg; ISO 11359 | |
| 線形熱膨脹系數(shù) - 流動 | 20.0 μm/m-°C @Temperature <=143 °C | 11.1 μin/in-°F @Temperature <=289 °F | Below Tg; ISO 11359 |
| 22.0 μm/m-°C @Temperature >=143 °C | 12.2 μin/in-°F @Temperature >=289 °F | Above Tg; ISO 11359 | |
| 導(dǎo)熱系數(shù) | 0.350 W/m-K | 2.43 BTU-in/hr-ft2-°F | Along flow; ISO 22007-4 |
| 0.300 W/m-K @Temperature 23.0 °C | 2.08 BTU-in/hr-ft2-°F @Temperature 73.4 °F | Average; ISO/CD 22007-4 | |
| 熔融溫度 | 343 °C | 649 °F | ISO 11357 |
| 載荷下熱變形溫度(1.8 MPa) | 315 °C | 599 °F | ISO 75-f |
| 玻璃化轉(zhuǎn)變溫度，Tg | 143 °C | 289 °F | Onset; ISO 11357 |
| 150 °C | 302 °F | Midpoint; ISO 11357 |
| 加工溫度 | <= 100 °C | <= 212 °F | Hopper Temperature |
| 射嘴溫度 | 380 °C | 716 °F | |
| 模具溫度 | 170 - 200 °C | 338 - 392 °F | |
| 干燥溫度 | 120 °C @Time 18000 sec | 248 °F @Time 5.00 hour | |
| 150 °C @Time 10800 sec | 302 °F @Time 3.00 hour |
上海韜盛塑化科技有限公司 對比點擊按鈕將公司加入對比列表，詳細對比不同公司差異上海韜盛塑化科技有限公司是一家集貿(mào)易與生產(chǎn)研發(fā)為一體的商貿(mào)公司，代理經(jīng)營各國各種型號塑膠原料，以及生產(chǎn)各種改性工程塑膠.本公司主更多上海韜盛塑化科技有限公司是一家集貿(mào)易與生產(chǎn)研發(fā)為一體的商貿(mào)公司，代理經(jīng)營各國各種型號塑膠原料，以及生產(chǎn)各種改性工程塑膠.本公司主要研發(fā)生產(chǎn):ABS、POM、PC、HIPSPMMA、PC/ABS、PA66、PPO、PBT、K膠.....特種工程料：PPS、LCP、PEI、TPX、PA9T、PA6T、PA12、PA46、PTFE、PCTG、TPEE、PEEK、PC/PBT...增強系列：PP、PPS、PPO、PBT、PA、ABS、POM工程系列：PPS、LCP、PTFE、PEI、PPO、PBT、PEEK、PA6T、9T、PA46通用系列：ABS、PC、POM、PMMA、PA66、EVA、PC/ABS、HIPS、GPPS、PP、PVC以上僅為我公司部分供貨目錄。如有需要，歡迎來電來函洽談。