| 密度 | 1.24 | g/cm3 | ASTM D1505 |
| 薄膜厚度 (經(jīng)測(cè)試) | 25 | μm | |
| 割線模量 (MD: 25 μm) | 3450 | μm | ASTM D882 |
| (TD: 25 μm) | 3790 | μm | ASTM D882 |
| 抗張強(qiáng)度 (MD: 屈服, 25 μm) | 103 | μm | ASTM D882 |
| (TD: 屈服, 25 μm) | 145 | μm | ASTM D882 |
| 伸長(zhǎng)率 (MD: 斷裂, 25 μm) | 180 | % | ASTM D882 |
| (TD: 斷裂, 25 μm) | 100 | % | ASTM D882 |
| 埃爾曼多夫抗撕強(qiáng)度 (MD: 25 μm) | 17 | g | ASTM D1922 |
| (TD: 25 μm) | 14 | g | ASTM D1922 |
| 透氧率 | 550 | cm3·mm/m2/atm/24 hr | ASTM D3985 |
| 水氣透過(guò)率 | 330 | g·mm/m2/atm/24 hr | ASTM F1249 |
| 玻璃轉(zhuǎn)化溫度 (DSC) | 57.8 | ℃ | DSC |
| 熔融溫度 | 160 | ℃ |
| 光澤度 (20℃, 25.4 μm) | 90 | ASTM D2457 | |
| 霧度 (25.4 μm) | 2.1 | % | ASTM D1003 |