| 密度 | 1.24 | g/cm3 | ASTM D1505 |
| 薄膜厚度 (經(jīng)測(cè)試) | 25 | μm | |
| 割線模量 (MD: 25 μm) | 3310 | MPa | ASTM D882 |
| (TD: 25 μm) | 3860 | MPa | ASTM D882 |
| 抗張強(qiáng)度 (MD: 屈服, 25 μm) | 110 | MPa | ASTM D882 |
| (TD: 屈服, 25 μm) | 145 | MPa | ASTM D882 |
| (MD: 斷裂, 25 μm) | 110 | MPa | ASTM D882 |
| 伸長(zhǎng)率 (MD: 斷裂, 25 μm) | 160 | % | ASTM D882 |
| (TD: 斷裂, 25 μm) | 100 | % | ASTM D882 |
| 埃爾曼多夫抗撕強(qiáng)度 (MD: 25 μm) | 15 | g | ASTM D1922 |
| (TD: 25 μm) | 13 | g | ASTM D1922 |
| 透氧率 | 220 | cm3·mm/m2/atm/24 hr | ASTM D3985 |
| 水氣透過(guò)率 | 130 | g·mm/m2/atm/24 hr | ASTM F1249 |
| Spencer Impact | 2.50 | J | |
| 二氧化碳傳輸速率 | 76 | cm3·mm/m2/atm/24 hr | ASTM D1434 |
| 熔融溫度 | 135 | ℃ |
| 光澤度 (20℃) | 90 | ASTM D2457 | |
| 霧度 | 2.1 | % | ASTM D1003 |