| 吸水率 (浸水24hrs后增重) | 0.3 | % | ASTM D-570 |
| 熔體流動(dòng)速率 | 3.7/3.5 | g/min | ASTM D-1238 |
| 折射率Nd | 1.49 | ASTM D-542 | |
| 比重 | 1.19 | ASTM D-792 | |
| 透光率 | 92 | % | ASTM D-1003 |
| 霧度 | <2 | % | |
| 成形收縮率 ((冷模/冷件),48hrs) | 0.2-0.6 | % | ASTM D-935 |
| 彎曲模數(shù) | 32000 | kgf/cm | ASTM D-790 |
| IZOD缺口沖擊強(qiáng)度 (落錘(15.2*15.2*0.3cm)重1.4kg半徑0.64cm) | 1.2(12.3) | kgf.cm/cm(J/m) | ASTM D256 |
| 拉伸強(qiáng)度 (初級(jí)應(yīng)變速率0.1cm/cm/min) | 720(70) | kgf/cm(MPa) | ASTM D-638 |
| 彎曲強(qiáng)度 (橫跨比=16) | 1050(103) | kgf/cm(MPa) | ASTM D-790 |
| 洛氏硬度 | 97 | M scale | ASTM D-758 |
| 使用溫度范圍 (與殘余應(yīng)力大小有關(guān)) | 82-102 | ||
| 玻璃化轉(zhuǎn)變溫度Tg | 108 | ℃ | |
| 熱變形溫度 | 102 | ℃ | ASTM D-648 |
| 維卡軟化點(diǎn) | ASTM D-1525 | ||
| (50℃/hr,1kg) | 111 | ℃ | |
| (50℃/hr,5kg) | 104 | ℃ |