| 熔體流動速率 | 3.5 | g/10min | ASTM D-1238 |
| 吸水率 (浸水24hrs后增重) | 0.3 | % | ASTM D-570 |
| 折射率Nd | 1.49 | ASTM D-542 | |
| 成形收縮率 ((冷模/冷件),48hrs) | 0.2-0.6 | % | ASTM D-935 |
| 霧度 | <2 | % | |
| 洛氏硬度 | 97 | ASTM D-758(M級) | |
| 透光率 | 92 | % | ASTM D-1003 |
| 比重 | 1.19 | ASTM D-792 |
| 沖擊強(qiáng)度 (Izod 研磨缺口) | 1.2(12.3) | kgf-cm/cm(J/m) | ASTM D256 |
| 彎曲強(qiáng)度 (橫跨比=16) | 1050(103) | kgf/cm(MPa) | ASTM D-790 |
| 彎曲模數(shù) | 32000 | kgf/cm | ASTM D-790 |
| 沖擊強(qiáng)度 (落錘(15.2×15.2×0.3cm重1.4kg半徑0.64cm)) | 14(1.4) | kg-cm(J) | ASTM D256 |
| 拉伸強(qiáng)度 (初級應(yīng)變速度0.1cm/cm/min) | 720(70) | kgf/cm(MPa) | ASTM D-638 |
| 維卡軟化點(diǎn) | ASTM D-1525.未退火 | ||
| (50℃/hr,1kg) | 111 | ℃ | |
| (50℃/hr,5kg) | 104 | ℃ | |
| 使用溫度范圍 (與殘余應(yīng)力大小有關(guān)) | 85-102 | ℃ | |
| 熱變形溫度負(fù)荷.退火 (2℃/min,18.6kgf/cm) | 102 | ℃ | ASTM D-648 |
| 玻璃化轉(zhuǎn)變溫度 (Tg) | 108 | ℃ |