| 密度 | 1.15 | 23度比重 | ASTM D792 |
| 24小時吸水率 | 0.40 | % | ASTM D570 |
| 熔流率 | 3.3 | g/10 min | ASTM D1238 |
| 收縮率 (平行流動方向) | 0.0030 - 0.0080 | cm/cm | ASTM D955 |
| 抗壓強度 | 41.4 | MPa | ASTM D695 |
| 拉伸模量 | 1650 | MPa | ASTM D638 |
| 斷裂點拉伸強度 | 37.2 | MPa | ASTM D638 |
| 彎曲模量 | 1860 | MPa | ASTM D790 |
| 斷裂彎曲強度 | 71 | MPa | ASTM D790 |
| 斷裂點伸長率 | 35 | % | ASTM D638 |
| 缺口沖擊強度 | 53.4 | J/m | ASTM D256 |
| 熱傳導 | -- | W/m/K | ASTM C177 |
| 維卡軟化溫度 (Rate A, Loading 1 (10 N)) | 82.8 | ℃ | ASTM D1525 |
| 熱變形溫度 (264 psi.未退火) | 79.4 | ℃ | ASTM D648 |
| UL阻燃等級 (1.47 mm) | HB | UL 94 |
| 折射率 | -- | ASTM D542 | |
| 透光度 | 91.0 | % | ASTM D1003 |
| 霧度 | 3.0 | % | ASTM D1003 |