| 吸水率 (浸水24hrs后増重) | 0.3 | % | ASTM D-570 |
| 熔體流動(dòng)速率 | 2 | g/min | ASTM D-1238 |
| 模縮系數(shù) | 0.4-0.8 | % | ASTM D-955 |
| 霧度 | <2 | % | |
| 比重 | 1.18 | ASTM D-792 | |
| 難燃性能 | HB | Class | UL 94 |
| 折射率Nd | 1.49 | ASTM D-542 | |
| 透光率 | 93 | % | ASTM D-1003 |
| 彎曲強(qiáng)度 (橫夸比=16) | 1460(143) | kgf/cm(MPa) | ASTM D-790 |
| 彎曲模量 | 34000 | kgf/cm | ASTM D-790 |
| 拉伸強(qiáng)度 (初級(jí)應(yīng)變速率0.1cm/cm/min) | 767(75) | kgf/cm(MPa) | ASTM D-638 |
| 洛氏硬度 | 99 | ASTM D-758(M級(jí)) | |
| 沖擊強(qiáng)度 | ASTM D-256 | ||
| (落錘(15.2*15.2*0.3cm)重1.4kg 半徑0.64cm) | 14(1.6) | kg-cm(J) | |
| (Lzod 研磨缺口) | 1.5(14.7) | kgf-cm/cm(J/m) |
| 熱變形溫度 | 103 | ℃ | ASTM D-648 |
| 維卡軟化點(diǎn) (50℃/hr,1kg) | 235 | F | ASTM D-1525 |
| 使用溫度范圍 (與殘余應(yīng)力大小有關(guān)) | 85-105 | ||
| 維卡軟化點(diǎn) (未退火) | 113 | ℃ | ASTM D-1525 |