| 比重 | 1.15 | g/cm3 | JIS K7112 |
| 熔體流動(dòng)速率 (230℃/3.8Kg) | 1.9 | g/10 min | JIS K7210 |
| 收縮率 (流動(dòng)) | 0.40-0.70 | % | ASTM D955 |
| 吸水率 (24hr) | 0.40 | % | JIS K7209 |
| 洛氏硬度 (M 計(jì)秤) | 50 | JIS K7202 |
| 抗張強(qiáng)度 | 38.0 | MPa | JIS K7113 |
| 伸長(zhǎng)率 (斷裂) | 90 | % | JIS K7113 |
| 彎曲模量 | 1800 | MPa | JIS K7203 |
| 彎曲強(qiáng)度 | 64.0 | MPa | JIS K7203 |
| 簡(jiǎn)支梁缺口沖擊強(qiáng)度 | 5.6 | kJ/m2 | JIS K7110 |
| 熱變形溫度 (1.8MPa.退火) | 87.0 | ℃ | JIS K7207 |
| 維卡軟化溫度 | 97.0 | ℃ | JIS K7206 |
| 線性膨脹系數(shù) (流動(dòng)) | 0.000090 | cm/cm/℃ | ASTM D696 |
| 表面電阻率 | >1.0E+16 | ohm | JIS K6911 |
| 體積電阻率 | >1.0E+15 | ohm·cm | JIS K6911 |
| 介電常數(shù) | 3.10 | JIS K6911 | |
| 損耗因數(shù) | 0.04 | JIS K6911 | |
| 絕緣電阻 | ＞1.0E+15 | ohm | JIS K6911 |
| 燃燒速率 | 30 | mm/min | ASTM D63 |
| UL阻燃等級(jí) (1.59mm,AII Colors) | HB | UL 94 |
| 折射率 | 1.490 | JIS K7105 | |
| 透射率 | 91.0 | % | JIS K7105 |
| 霧度 | 2.0 | % | JIS K7105 |
| 彎曲剛度 | ＞8.0 | % | JIS K7203 |
| 絕緣強(qiáng)度 | 20.0 | KV/min | JIS K6911 |