| 霧度2 (40 mil) | 76.1 | % | ASTM D-1003 |
| 硬度2 (Shore A,15 sec) | >90 | ASTM D-2240 | |
| 密度 | 0.902 | g/cm | ExxonMobil Method |
| 熔體流動速率 | 2.5 | g/10 min | ExxonMobil Method |
| 硬度2 (Shore D,15 sec) | 36.8 | ASTM D-2240 | |
| 熔融指數 | 1.1 | g/10 min | ExxonMobil Method |
| 彎曲模量 (1% secant) | 9842(67.9) | psi(MPa) | ASTM D-790 |
| 沖擊強度 | ASTM D-256 | ||
| (23℃) | No Break | ft-lb/in(J/m) | |
| (-40℃) | No Break | ft-lb/in(J/m) | |
| 拉伸強度3 (@Break) | No Break | psi(MPa) | ASTM D-638 |
| 拉伸率 (@Break) | No Break | % | ASTM D-638 |
| 高熔體溫度 | 206.4(96.9) | ?H(℃) | ExxonMobil Method |
| 維卡軟化點2 | ASTM D-1525 | ||
| (1000g) | 182.7(83.7) | ℉(℃) | |
| (200g) | 205.2(96.2) | ℉(℃) |
| 拉應力5 (@ Elongation) | 1780(12.3) | psi(MPa) | ASTM D-412 |
| 拉伸率 (@Break) | 1144 | % | ASTM D-412 |
| 抗扯強度 | 508.5(89.1) | lb-in(kN/m) | ASTM D-624 |
| 拉伸強度 (@Peak) | 4454(30.7) | psi(MPa) | ASTM D-412 |
| 門尼粘度ML(1+4) (125℃) | 3.9 | Torgue Units | ASTM D-1646 |
| 抗環(huán)境應力開裂性 | >1000 | hr | ASTM D-1693 |
| 拉應力5 (@300% Elongation) | 2115(14.6) | psi(MPa) | ASTM D-412 |