| 熔體流動(dòng)速率 | 0.9 | g/10 min | ExxonMobil Method |
| 硬度2 (Shore A,15 sec) | 65 | ASTM D-2240 | |
| 熔融指數(shù) | 0.5 | g/10 min | ExxonMobil Method |
| 密度 | 0.868 | g/cm | ExxonMobil Method |
| 霧度2 | 8@50mil | % | ASTM D-1003 |
| 拉伸強(qiáng)度3 (@Break) | >1100(>7) | psi(MPa) | ASTM D-638 |
| 彎曲模量 (1% secant) | 1676(12) | psi(MPa) | ASTM D-790 |
| 高熔體溫度 | 127(53) | ℉(℃) | ExxonMobil Method |
| 門尼粘度ML(1+4) (125℃) | 31 | Torgue Units | ASTM D-1646 |
| 拉伸應(yīng)力5 (@300% Elongation) | 408(3) | psi(MPa) | ASTM D-412 |
| 抗扯強(qiáng)度 | 199(35) | lb/in(kN/m) | ASTM D-624 |
| 拉伸應(yīng)力5 (@ Elongation) | 298(2) | psi(MPa) | ASTM D-412 |