| 熔體流動(dòng)速率 | 6.5 | g/10 min | ASTM D-1238 |
| 硬度2 (Shore A,15 sec) | 80 | ASTM D-2240 | |
| 密度 | 0.882 | g/cm | ExxonMobil Method |
| 熔融指數(shù) | 3.0 | g/10 min | ASTM D-1238 |
| 硬度2 (Shore D,15 sec) | 30 | ASTM D-2240 | |
| 霧度2 | 11@50mils | % | ASTM D-1003 |
| 缺口沖擊強(qiáng)度 | ASTM D-3763 | ||
| (23℃) | 13.4(18.1)/18.6(25.2) | ft-lb/(J) | |
| (-40℃) | 12.3(16.7)/21.7(29.4) | ft-lb/(J) | |
| 拉伸強(qiáng)度3 (@Break) | No Break | psi(MPa) | ASTM D-638 |
| 彎曲模量 (1% secant) | 4104(28.3) | psi(MPa) | ASTM D-790 |
| 拉伸率 (@Break) | No Break | % | ASTM D-638 |
| 維卡軟化點(diǎn)2 (200g) | 163.0(72.8) | ℉(℃) | ASTM D-1525 |
| 高熔體溫度 | 163.9(73.3) | ℉(℃) | ExxonMobil Method |
| 門尼粘度ML(1+4) (125℃) | 11.5 | Torgue Units | ASTM D-1646 |
| 抗扯強(qiáng)度 | 247(42.0) | lb/in(kN/m) | ASTM D-624 |
| 拉伸應(yīng)力5 (@300% Elongation) | 5.8(4.0) | psi(MPa) | ASTM D-412 |
| 抗拉強(qiáng)度 (@Peak) | No Break | psi(MPa) | ASTM D-412 |
| 拉伸率 (@Break) | No Break | % | ASTM D-412 |
| 拉伸應(yīng)力5 (@ Elongation) | 464(3.2) | psi(MPa) | ASTM D-412 |