| 熔體流動速率 | 2.0 | g/10 min | ExxonMobil Method |
| 密度 | 0.902 | g/cm | ExxonMobil Method |
| 硬度2 (Shore D,15 sec) | 34 | ASTM D-2240 | |
| 熔融指數(shù) | 1.1 | g/10 min | ExxonMobil Method |
| 硬度2 (Shore A,15 sec) | 90 | ASTM D-2240 | |
| 門尼粘度ML(1+4) (125℃) | 18 | Torgue Units | ASTM D-1646 |
| 霧度2 | 80@50mil | % | ASTM D-1003 |
| 拉伸率 (@Break) | >2000(No Break) | % | ASTM D-638 |
| 抗扯強度 | 487(86) | lb/in(kN/m) | ASTM D-624 |
| 拉伸強度3 (@Break) | >3000(>21) | psi(MPa) | ASTM D-638 |
| 彎曲模量 (1% secant) | 12731(88) | psi(MPa) | ASTM D-790 |
| 維卡軟化點2 | ASTM D-1525 | ||
| (1000g) | 192(89) | ℉(℃) | |
| (200g) | 209(98) | ℉(℃) | |
| 高熔體溫度 | 209(98) | ℉(℃) | ExxonMobil Method |
| 耐環(huán)境應力開裂性 | >1000 | hr | ASTM D-1693 |