| 硬度2 | ASTM D-2240 | ||
| (Shore D,15 sec) | 43 | ||
| (Shore A,15 sec) | 85 | ||
| 熔融指數(shù) | 10.0 | g/10 min | ASTM D-1238 |
| 熔體流動(dòng)速率 | 25 | g/10 min | ASTM D-1238 |
| 密度 | 0.902 | g/cm | ExxonMobil Method |
| 霧度2 | 84@50mils | % | ASTM D-1003 |
| 彎曲模量 (1% secant) | 11.100(76.6) | psi(MPa) | ASTM D-790 |
| 沖擊強(qiáng)度 (-40℃) | No Break | ft-lb/in(J/m) | ASTM D-256 |
| 拉伸率 (@Break) | No Break | % | ASTM D-638 |
| 拉伸強(qiáng)度3 (@Break) | No Break | psi(MPa) | ASTM D-638 |
| 沖擊強(qiáng)度 (23℃) | No Break | ft-lb/in(J/m) | ASTM D-256 |
| 維卡軟化點(diǎn)2 (200g) | 183.4(84.1) | ℉(℃) | ASTM D-1525 |
| 高熔體溫度 | 205(96.0) | ℉(℃) | ExxonMobil Method |
| 門尼粘度ML(1+4) (125℃) | 4.6 | Torgue Units | ASTM D-1646 |
| 抗扯強(qiáng)度 | 423(74.1) | lb/in(kN/m) | ASTM D-624 |
| 拉伸強(qiáng)度 (@Peak) | No Break | psi(MPa) | ASTM D-412 |
| 拉伸應(yīng)力5 (@ Elongation) | 914(6.3) | psi(MPa) | ASTM D-412 |
| 拉伸率 (@Break) | No Break | % | ASTM D-412 |
| 拉伸應(yīng)力5 (@300% Elongation) | 972(6.7) | psi(MPa) | ASTM D-412 |