| 密度 | 0.870 | g/cm | ExxonMobil Method |
| 熔體流動速率 | 11.0 | g/10 min | ExxonMobil Method |
| 霧度2 | 5@50mils | % | ASTM D-1003 |
| 硬度2 (Shore A,15 sec) | 70 | ASTM D-2240 | |
| 熔融指數(shù) | 5.0 | g/10 min | ExxonMobil Method |
| 拉伸率 (@Break) | >2000(No Break) | % | ASTM D-638 |
| 拉伸強度3 (@Break) | >800(>5) | psi(MPa) | ASTM D-638 |
| 彎曲模量 (1% secant) | 1830(13) | psi(MPa) | ASTM D-790 |
| 高熔體溫度 | 147(64) | ℉(℃) | ExxonMobil Method |
| 拉伸應(yīng)力5 (@ Elongation) | 290(2) | psi(MPa) | ASTM D-412 |
| 抗扯強度 | 233(42) | lb/in(kN/m) | ASTM D-624 |
| 門尼粘度ML(1+4) (125℃) | 8 | Torgue Units | ASTM D-1646 |
| 拉伸應(yīng)力5 (@300% Elongation) | 363(3) | psi(MPa) | ASTM D-412 |