| 高熔體溫度 | 70 | ℃ | ASTM D3418 |
| 硬度 | ISO 868 | ||
| (Shore D) | 29 | ||
| (Shore A) | 85 | ||
| 脆化溫度 | <-75 | ℃ | ASTM D746 |
| 熔融熱 | 105 | J/g | ASTM D3418 |
| 密度 (23℃) | 882 | kg/cm | ISO 1183 |
| 維卡軟化點(diǎn) (at 10 N) | 55 | ℃ | ISO 306 |
| 熔體流動(dòng)速率 (2.16kg/190℃) | 1.1 | dg/min | ISO 1133 |
| 斷裂拉伸強(qiáng)度 | 24 | MPa | ISO 527-2 |
| 耐環(huán)境應(yīng)力開(kāi)裂性 | >1000 | hr | ASTM D-1693 |
| 缺口沖擊強(qiáng)度 (@23℃ and @-40℃) | No Break | J/M | ASTM D256 |
| 彎曲模量 | 30 | MPa | ISO 178 |
| 斷裂拉伸率 | 1750 | % | ISO 527-2 |
| 門尼粘度ML(1+4) (125℃) | 16.5 | Torgue Units | ASTM D-1646 |
| 沖擊強(qiáng)度 | >18 | g/u | ASTM D4272 |
| 霧度 | 2.2 | % | ASTM D1003(A) |
| 抗擊穿能量 | 1500 | MJ/mm | Internal b |
| 模量 (1% secant) | 24/25 | MPa | ISO 1184(F) |
| 表面光澤 (45℃) | 84 | ASTM 2457 | |
| 大抗擊穿壓力 | 125 | MPa | Internal b |