| 比重 | 0.870 | g/cm | ASTM D792 |
| 熔流率 (190℃/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 門尼粘度 (ML 1+4, 121℃) | 24 | MU | ASTM D1646 |
| 硬度計硬度 | |||
| (邵氏 A, 1 秒, 模壓成型) | 73 | ASTM D2240 | |
| (邵氏 D, 1 秒, 模壓成型) | 22 | ASTM D2240 | |
| 拉伸模量 ( 正割 (模壓成型)) | 2.90 | MPa | ASTM D638 |
| 抗張強度 (斷裂, 模壓成型) | 9.76 | MPa | ASTM D638 |
| 伸長率 (斷裂, 模壓成型) | 810 | % | ASTM D638 |
| 彎曲模量 | |||
| (1% 正割: 模壓成型) | 14.3 | MPa | ASTM D790 |
| (2% 正割: 模壓成型) | 13.1 | MPa | ASTM D790 |
| 撕裂強度 | 40.0 | kN/m | ASTM D624 |
| 玻璃轉化溫度 | -52.0 | ℃ | Internal Method |
| 維卡軟化溫度 | 45.0 | ℃ | ASTM D1525 |
| 溶融溫度 | 60.0 | ℃ | Internal Method |
| 結晶峰溫 | 45.0 | ℃ | Internal Method |