| 比重 | 0.902 | g/cm | ASTM D792 |
| 熔流率 (190℃/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 門尼粘度 (ML 1+4, 121℃) | 20 | MU | ASTM D1646 |
| 硬度計硬度 | |||
| (邵氏 A, 1 秒, 模壓成型) | 89 | ASTM D2240 | |
| (邵氏 D, 1 秒, 模壓成型) | 42 | ASTM D2240 | |
| 拉伸模量 ( 正割 (模壓成型)) | 8.00 | MPa | ASTM D638 |
| 抗張強度 (斷裂, 模壓成型) | 24.8 | MPa | ASTM D638 |
| 伸長率 (斷裂, 模壓成型) | 660 | % | ASTM D638 |
| 彎曲模量 | |||
| (1% 正割: 模壓成型) | 83.1 | MPa | ASTM D790 |
| (2% 正割: 模壓成型) | 81.5 | MPa | ASTM D790 |
| 撕裂強度 | 91.2 | kN/m | ASTM D624 |
| 玻璃轉(zhuǎn)化溫度 | -31.0 | ℃ | Internal Method |
| 維卡軟化溫度 | 89.0 | ℃ | ASTM D1525 |
| 溶融溫度 | 99.0 | ℃ | Internal Method |
| 結(jié)晶峰溫 | 84.0 | ℃ | Internal Method |