| 密度 | 885 | g/cm | ASTM D1505 |
| 表面硬度 | 87 | shore A | JIS K6253 |
| 熔融指數(shù) | |||
| (190℃) | 0.5 | g/10min | ASTM D1238 |
| (191℃) | 0.9 | g/11min | ASTM D1239 |
| 斷裂強(qiáng)度 | 35< | Mpa | JIS K7113 |
| 斷裂伸長(zhǎng) | 800< | % | JIS K7114 |
| 扭曲剛性 | 9 | Mpa | ASTM D1043 |
| 熔點(diǎn) | 66 | ℃ | ASTM D2117 |
| 維卡軟化點(diǎn) | 62 | ℃ | ASTM D1525 |
| 脆化溫度 | -70> | ℃ | ASTM D748 |
| 體積電阻系數(shù) | 10< | Ω-CM | ASTM D257 |
| 介電常數(shù) | 2.2-2.4 | ASTM D150 | |
| 介電正接 | 5*10-4> | ASTM D150 |