| 比重 | 0.902 | g/cm3 | ASTM D792 |
| 熔流率 (190℃/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| 薄膜厚度 (經(jīng)測(cè)試) | 51 | μm | |
| 膜刺穿強(qiáng)度 (51 μm) | 8.81 | J | Internal Method |
| 膜刺穿力 (51 μm) | 82.5 | N | Internal Method |
| 膜耐刺穿性 (51 μm) | 22.3 | J/cm3 | Internal Method |
| 割線模量 (2% 正割, MD : 51 μm) | 91.7 | MPa | ASTM D882 |
| (2% 正割, TD : 51 μm) | 92.4 | MPa | ASTM D882 |
| 抗張強(qiáng)度 (MD : 屈服, 51 μm) | 7.24 | MPa | ASTM D882 |
| (TD : 屈服, 51 μm) | 6.89 | MPa | ASTM D882 |
| (MD : 斷裂,51 μm) | 58.6 | MPa | ASTM D882 |
| (TD : 斷裂,51μm) | 44.7 | MPa | ASTM D882 |
| 伸長(zhǎng)率 (MD : 斷裂, 51 μm) | 620 | % | ASTM D882 |
| (TD : 斷裂, 51 μm) | 630 | % | ASTM D882 |
| 落錘沖擊 (51 μm) | > 830 | g | ASTM D1709B |
| 埃爾曼多夫抗撕強(qiáng)度 (MD : 51 μm) | 550 | g | ASTM D1922 |
| (TD : 51 μm) | 720 | g | ASTM D1922 |
| 始封溫度 (51 μm) | 85.0 | ℃ | Internal Method |
| 維卡軟化溫度 | 86.0 | ℃ | ASTM D1525 |
| 溶融溫度 (DSC) | 99.0 | ℃ | Internal Method |
| 光澤度 (20°, 50.8 μm) | 141 | ASTM D2457 | |
| 透明度 (50.8 μm) | 83.0 | ASTM D1746 | |
| 霧度 (50.8 μm) | 1.1 | % | ASTM D1003 |