| 吸水率 | ASTM D-570 | ||
| (24小時.73℉) | 0.250 | % | |
| (平衡,73℉) | 1.25 | % |
| 泰伯磨耗量 | 10 | mg/1000次 | ASTM D-1044 |
| 模具收縮率 | 5-7 | in/inE-3 | ASTM D-955 |
| 固體比重 | 1.27 | ASTM D-792 |
| 洛氏硬度 | 109 | Psi | ASTM D-785 |
| 屈服撓曲強度 | 22000 | Psi | ASTM D-790 |
| IZOD無缺口沖擊強度 | 25.0 | ft-lb/in | ASTM D-4812 |
| 屈服抗拉伸長 | 7.0 | % | ASTM D-638 |
| 屈服抗拉強度 | 15200 | Psi | ASTM D-638 |
| IZOD缺口沖擊強度 | 0.6 | ft-lb/in | ASTM D-256 |
| 撓曲模量 | 480000 | Psi | ASTM D-790 |
| 斷裂抗拉伸伸長 | 60.0 | % | ASTM D-638 |
| 體積電阻率 | 1×10 | Ω.cm | ASTM D-257 |
| 介電常數(shù) | ASTM D-150 | ||
| 損耗因數(shù) (1KHz) | 0.0013 | ASTM D-150 | |
| 介電強度 (62mils) | 830 | V/mil | ASTM D-149 |
| 熱指數(shù) | UL746B | ||
| 170 | ℃ | ||
| 170 | ℃ | ||
| 170 | ℃ | ||
| 熱變形溫度 (66Psi) | 405 | ℉ | ASTM D-648 |
| 線膨脹系數(shù) | ASTM E-831 | ||
| 3 | E-5/in/in℉ | ||
| - | E-5/in/in℉ | ||
| 維卡軟化點 | 426 | ℉ | ASTM D-1525 |
| 熱變形溫度 (264Psi) | 387 | ℉ | ASTM D-648 |
| 燃燒性 | V-0 | class | UL 94 |