| 密度 | 1.27 | g/cm3 | ASTM D1505 |
| 收縮率 - 流動(dòng) | 0.20 到 0.50 | % | ASTM D955 |
| 吸水率(24hr) | 0.13 | % | ASTM D570 |
| 洛氏硬度(R級(jí)) | 108 | ASTM D785 |
| 抗張強(qiáng)度 | |||
| 屈服1 | 50.0 | MPa | ASTM D638 |
| 屈服 | 50.0 | MPa | ISO 527-2/50 |
| 斷裂2 | 29.0 | MPa | ASTM D638 |
| 斷裂 | 29.0 | MPa | ISO 527-2/50 |
| 伸長(zhǎng)率 | |||
| 屈服3 | 4.5 | % | ASTM D638 |
| 屈服 | 4.5 | % | ISO 527-2/50 |
| 斷裂4 | 180 | % | ASTM D638 |
| 斷裂 | 180 | % | ISO 527-2/50 |
| 彎曲模量5 | 2100 | MPa | ASTM D790, ISO 178 |
| 彎曲強(qiáng)度6 | 69.0 | MPa | ASTM D790, ISO 178 |
| 懸壁梁缺口沖擊強(qiáng)度 | |||
| 23°C | 110 | J/m | ASTM D256 |
| 23°C | 12 | kJ/m2 | ISO 180 |
| 載荷下熱變形溫度 | |||
| 0.45 MPa, 未退火 | 70.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, 未退火 | 62.0 | °C | ASTM D648, ISO 75-2/A |
| UL 阻燃等級(jí)(1.60 到 1.70 mm) | HB | UL 94 |
| 透射率 | 90.0 | % | ASTM D1003 |
| 霧度 | < 1.0 | % | ASTM D1003 |
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 1.3 mm/min |