| 吸水率 (飽和(23℃)) | 7.1 | % | ASTM D-570 |
| 比重 | 1.22 | ASTM D-792 |
| 洛氏硬度R (DAM) | R122 | ASTM D-785 | |
| 洛氏硬度M (DAM) | M95 | ASTM D-785 | |
| 斷裂伸長(zhǎng)率 (23℃,DAM) | 2 | % | ASTM D-638 |
| 撓曲模量 (23℃,DAM) | 4826 | MPa | ASTM D-790 |
| 埃佐沖擊強(qiáng)度 (23℃,DAM) | 48 | j/m | ASTM D-256 |
| 斷裂伸長(zhǎng)率 (23℃,50%RH) | 8 | % | ASTM D-638 |
| 撓曲模量 (23℃,50%RH) | 2758 | MPa | ASTM D-790 |
| 埃佐沖擊強(qiáng)度 (23℃,50%RH) | 53 | j/m | ASTM D-256 |
| 洛氏硬度R (50%RH) | R113 | ASTM D-785 | |
| 洛氏硬度M (50%RH) | M84 | ASTM D-785 | |
| 撓曲強(qiáng)度 (23℃,DAM) | 165 | MPa | ASTM D-790 |
| 泰伯磨耗量 (50%RH) | 12 | cycles | |
| 擠剪強(qiáng)度 (23℃,DAM) | 76 | MPa | ASTM D-732 |
| 拉伸強(qiáng)度 | ASTM D-638 | ||
| (23℃,50%RH) | 82.7 | MPa | |
| (23℃,DAM) | 103.4 | MPa |
| 熔點(diǎn) | ASTM D-789 | ||
| (50%RH) | 255 | ℃ | |
| (DAM) | 255 | ℃ | |
| 線性熱膨脹系數(shù) | 2.7×10-5 | m/m/℃ | ASTM D-696 |
| 熱畸變溫度 (1.8MPa) | 243 | ℃ | ASTM D-648 |