| 吸水率 | ASTM D-570 | ||
| (24小時(shí)浸漬(23℃)) | 0.6 | % | |
| (飽和(23℃)) | 4.7 | % |
| 比重 | 1.51 | ASTM D-792 |
| 斷裂伸長(zhǎng)率 | ASTM D-638 | ||
| (23℃,50%RH) | 3 | % | |
| (23℃,DAM) | 2 | % | |
| 撓曲模量 (23℃,DAM) | 11032 | MPa | ASTM D-790 |
| 埃佐沖擊強(qiáng)度 (23℃,DAM) | 133 | j/m | ASTM D-256 |
| 拉伸強(qiáng)度 | ASTM D-638 | ||
| (23℃,50%RH) | 144.7 | MPa | |
| (23℃,DAM) | 206.8 | MPa | |
| 擠剪強(qiáng)度 (23℃,DAM) | 93 | MPa | ASTM D-732 |
| 洛氏硬度M (DAM) | M103 | ASTM D-785 | |
| 撓曲模量 (23℃,50%RH) | 8274 | MPa | ASTM D-790 |
| 埃佐沖擊強(qiáng)度 (23℃,50%RH) | 186 | j/m | ASTM D-256 |
| 撓曲強(qiáng)度 (23℃,DAM) | 285 | MPa | ASTM D-790 |
| 介電強(qiáng)度 ((分步法)DAM) | 410 | volts/mil | ASTM D-149 |
| 熱畸變溫度 (1.8MPa) | 252 | MPa | ASTM D-648 |
| 熔點(diǎn) (50%RH) | 255 | ℃ | ASTM D-789 |
| 線性熱膨脹系數(shù) | 2.2×10-5 | m/m/℃ | ASTM D-696 |
| 熔點(diǎn) (DAM) | 255 | ℃ | ASTM D-789 |