| 熔體流動速率 (230℃ 2.16kg) | 10 | g/10min | ASTM D-1238 |
| 比重 | 1.12 | ASTM D-792 | |
| 成型收縮率 (2mm(t)) | 1.0-1.4 | % | SGC Method |
| 屈服拉伸強(qiáng)度 (50mm/min) | 33 | MPa | ASTM D-638 |
| 斷裂伸長率 (50mm/min) | 40 | % | ASTM D-638 |
| 彎曲強(qiáng)度 | 33 | MPa | ASTM D-747 |
| 彎曲模量 | 3432 | MPa | ASTM D-790 |
| IZOD沖擊強(qiáng)度 (23℃) | 5.0 | kg·cm/cm | ASTM D-256 |
| 洛氏硬度 (23℃) | 91 | R scale | ASTM D-785 |
| 熱變形溫度 (4.6kg/cm(1/4")) | 142 | ℃ | ASTM D-648 |
| 維卡軟化點(diǎn) (1kg) | 153 | ℃ | ASTM D-1525 |
| 阻燃性 | UL 94 | ||
| (1/8") | HB | ||
| (1/16") | HB |